US 4,229,224 AGranted

Cementitious compositions

AssigneeImperial Chemical Industries PLC

InventorsDavid G. Dawson, Desmond W. J. Osmond, Maurice W. Skinner, Edmund J. West

Life of this patent

Estimating the term…

Loading patent…

Abstract

In U.S. Pat. No. 4,070,199 we have described cured polymer-containing cementitious compositions of high modulus of rupture. The cured compositions are made by curing the product of subjecting to a homogenization process comprising high shear mixing (e.g. extrusion or calendering) the ingredients hydraulic cement, water and a selected water-dispersible polymer. The polymer is selected by a test which determines thermally its effect on the cement hydration reaction. The present invention describes the use in similar compositions of a class of water-dispersible acidic polymer, not selected by the above-mentioned test, which contains a specified proportion of carboxyl groups. Shaped products comprised of the new cured compositions of high modulus of rupture are useful, for example, in building applications where previously it was necessary to employ asbestos in admixture with the cement.

Claims13

Dependent claims

A homogeneous uncured cementitious composition which comprises the ingredients:

(a) a hydraulic cement,
(b) water, and
(c) a water-dispersible polymer selected from those polymers which contain carboxyl groups and which have total carboxyl content equivalent to at least 50 mg KOH/g of polymer, and which have a pK.sub.a in the range of 3-10;
and wherein:
(i) the ratio of water to hydraulic cement is in the range of 10-28 parts by weight of water to 100 parts of hydraulic cement:
(ii) the ratio of the water-dispersible polymer to hydraulic cement is in the range 0.1-10.0 parts by weight of water-dispersible polymer to 100 parts by weight of hydraulic cement;
and
(iii) the water-dispersible polymer is further selected with reference to the hydraulic cement and to the selected proportions of water and hydraulic cement for its suitability to facilitate homogenisation and to yield on homogenisation a product which can be shaped under pressure and which product is shape retaining;
and wherein the ingredients (a), (b) and (c), have been jointly subjected to a homogenisation process and, optionally, are shaped such that on curing and drying, the homogeneous uncured composition yields a cured, dried and optionally shaped cementitious material having a modulus of rupture greater than 15 MN/m.sup.2.

6 more elements