Gypsum with resin binder
AssigneeMary W. White
InventorDuane W. Flake
Life of this patent
Estimating the term…
Abstract
A building material prepared by combining a cementitious slurry with an uncured foamed resin and allowing the mixture to cure and harden. The resulting product is primarily cementitious material held in position with a hardened resin binder.
Claims6
A building material formed from the combination and curing of a hard water slurry of a cementitious material and hard water detergent containing resinous foam wherein the resin is selected from the group consisting of urea-formaldehyde, phenol-formaldehyde and melamine-formaldehyde resins and consisting of about 99.5 to 85 percent of said cementitious material intimately combined with from about 0.5 to 15 percent by weight of said foamed resin and also containing calcium and magnesium ions from said hard water and detergent from said resinous foam.
A method of preparing a building material consisting of a cementitious material intimately combined with a foamed resin comprising the steps of,
- (a) preparing an aqueous resin with hard water, having a resin concentration of about 15 to 25 weight percent,
- (b) preparing a detergent solution with hard water having a detergent concentration of about 1 to 3 weight percent,
- (c) preparing a slurry by mixing a finely divided cementitious material with water wherein the weight ratio of cementitious material to water is about 0.75:1 to 1.25:1,
- (d) combining the aqueous resin solution and detergent solutions wtih aeration at a detergent to resin solution ratio of 0.5:1 to 1.5:1 thereby forming a resin foam,
- (e) intimately combining the resin foam with the cementitious material slurry at a volumetric ratio of foam to slurry of about 0.5:1 to 6:1 to form a foam slurry mixture and,
- (f) placing said foam slurry in a mold until cured.
Dependencies are inferred from the claim text.