Heat-resistant alloy for welded structures
AssigneeNippon Steel Corporation
InventorsYuzo Hosoi, Noboru Shinoda, Yutaka Tsuchida, Shozo Sekino, Mizuo Sakakihara, Shoji Murota
Life of this patent
Estimating the term…
Abstract
A heat-resistant alloy suitable for welded structures, particularly suitable for nuclear reactors, and free from the adverse effect of the cobalt used therein, which alloy has a basic composition comprising; 0.01-0.2% C, not more than 0.50% Si, not more than 0.50% Mn, 10 to 25% Cr, not more than 0.030% B, not more than 0.50% Zr, not more than 20% of (Mo+1/2W), 0.001 to 0.04% Y, not more than 2.0% Al, and not more than 1.0% Ti, with the balance being Ni and unavoidable impurities.
Claims2
A heat-resistant alloy consisting of:
- C:
- 0.01-0.20%
- Si:
- not more than 0.50%
- Mn:
- not more than 0.50%
- Cr:
- 10 to 25%
- B:
- not more than 0.030%
- Zr:
- not more than 0.50%
- Mo+1/2W:
- 5 to 20%
- W:
- 10 to 20% when Mo is less than 10%
- Mo:
- 10 to 16% when W is 3 to 10%
- Y:
- 0.001 to 0.04%
- Al:
- not more than 2.0%
- Ti:
- not more than 1.0%
- one or more of Ce, La, Mg, Ca, Nb, Ta, V and Hf in the following amount:
- Ce, La, Mg, Ca:
- 0.001 to 0.050% for each and not more than 0.1% in total
- Nb, Ta, V, Hf:
- 0.001 to 3.0% for each and not more than 3.0% in total,
- with the balance being Ni and unavoidable impurities wherein Y.sub.E is defined in the equation
- Y.sub.E =(Y)%+1/5(Zr)%-1.85(S)-3.7(O)%
- wherein (Y), (Zr), (S) and (O) represent the amount of those respective elements present in the alloy on a weight basis, is in the range from about -0.01 to 0.02%, the alloy possesses a creep rupture strength of more than about 300 hours and wherein the amount of tungsten and molybdenum is within the area defined by the points a, b, c, d, e, and f of FIG. 3 hereof.
A heat-resistant alloy for welded structures consisting of:
- C:
- 0.01-0.20%
- Si:
- not more than 0.50%
- Mn:
- not more than 0.50%
- Cr:
- 10 to 25%
- B:
- not more than 0.030%
- Zr:
- not more than 0.50%
- Mo+1/2W:
- 5 to 20%
- W:
- 10 to 20% when Mo is less than 10%
- Mo:
- 10 to 16 % when W is 3 to 10%
- Y:
- 0.001 to 0.04%
- Al:
- not more than 2.0%
- Ti:
- not more than 1.0%
- with the balance being Ni and unavoidable impurities wherein Y.sub.E is defined in the equation
- Y.sub.E =[Y]%+1/5[Zr]%-1.85[S]%-3.7[O]%
- wherein [Y], [Zr], [S], and [O] represent the amount of those respective elements present in the alloy on a weight basis, is in the range from about -0.01 to 0.02%, the alloy possesses a creep rupture strength of more than about 300 hours and wherein the amount of tungsten and molybdenum is within the area defined by the points a, b, c, d, e, and f of FIG. 3 hereof.