The present invention concerns the use of an aqueous solution of a silicate as a binder, particularly for hardening foundary molds and cores without the use of acid or other reagents to convert the silicate into a silican gel. According to the present invention, the silicate binder is not reacted but instead is rapidly dried, preferably enough within the space of 5 seconds to 10 minutes to reduce the initial water content of the aqueous silicate solution by at least 25%. In the preferred embodiments, this is achieved by forcing air through opposed porous sides of the mold box and the green sand contained therein. The present invention is also applicable to other composite forms such as the manufacture of plywood, particle board, briquettes, and the like.
Claims27
A method for manufacturing foundry molds or cores comprising
- (a) forming a green foundry sand around a pattern in a box having at least two air permeable faces, said sand comprising from 94 to 99.9% of a refractory foundry sand and having 0.1% to 6% by weight of an aqueous solution containing a soluble silicate as a binder, said silicate containing an alkali metal, ammonium, an ammonium complex, or mixtures thereof as a cation and a silicate as the anion, the anion to cation mole ratio being between 1:1 and 4:1, said soluble silicate further containing from 47 to 70% water;
- and
- (b) applying a differential pressure between said air permeable faces sufficient to force air therebetween at a rate sufficient in less than two minutes to remove at least 30% of the water contained in said aqueous solution and to harden the sand to an instant tensile strength in excess of that obtainable from hardening said green sand by carbon dioxide gasing.
A method for manufacturing foundry molds or cores comprising
- (a) forming a green foundry sand around a pattern in a box, said sand comprising from 94 to 99.9% of a refractory foundry sand and having 0.1% to 6% by weight of an aqueous solution containing a soluble silicate as a binder, said silicate containing an alkali metal, ammonium, an ammonium complex, or mixtures thereof as a cation and a silicate as the anion, the anion to cation mole ratio being between 1:1 and 4:1, said soluble silicate further containing from 47 to 70% water;
- (b) said box having an air permeable face with an open area of at least 1.5%;
- and
- (c) subjecting said green sand to a forced drying period not exceeding two minutes, during which at least 30% of the water in said aqueous solution is removed without reaction of said silicate and the core or mold is hardened to an instant tensile strength greater than that obtainable from hardening said green sand by carbon dioxide gasing.
In the manufacture of a foundry mold or core wherein a green sand is formed around a pattern in a box, said green sand being a refractory foundry sand containing a binder therefor, said green sand thereafter being hardened around said pattern in said mold box, the improvement which comprises
- (a) using as a binder for said green sand a soluble silicate containing an alkali metal, ammonium, an ammonium complex, or mixtures thereof as a cation and a silicate as the anion, the anion to cation mold ratio being between 1:1 and 4:1, said soluble silicate further containing from 47 to 70% water to form an aqueous solution, the amount of said aqueous solution being between 0.1% and 6% by weight of said green foundry sand;
- and
- (b) providing at least two air permeable faces in said box, said air permeable faces having an open area of at least 1.5%;
- and
- (c) applying a differential pressure between said air permeable faces sufficient to force air therebetween at a rate of at least 30 standard cubic feet per minute per 100 grams of sand, said air circulation rate being sufficient within two minutes to increase the solids content of said aqueous solution to at least 54% and to harden the mold to an instant tensile strength in excess of that obtainable from said sand by carbon dioxide gasing.
A method for forming a desired shape from a particulate material comprising
- (a) forming a green mixture of said particulate material and an aqueous solution of a soluble silicate as a binder into a mold having said desired shape and at least two air permeable faces, said green mixture containing from 6 to 100 parts by weight of said soluble silicate for each 100 parts by weight of said particulate material, the amount of said aqueous solution being sufficient, when combined with said particulate material, to form a porous, plastic mass, said soluble silicate containing an alkali metal, ammonium, an ammonium complex, or mixtures thereof, as a cation and a silicate as the anion, the anion to cation mole ratio being between 1:1 and 4:1, said soluble silicate further containing from 47 to 70% water;
- and
- (b) applying a differential pressure between said air permeable faces sufficient to force air therebetween at a rate sufficient, within two minutes, to remove at least 30% of the water from said aqueous solution containing a soluble silicate, and to harden the green mixture to a tensile strength of at least 20 pounds per square inch.
A method for forming a desired shape from a particulate material comprising
- (a) molding a green mixture of said particulate material and an aqueous solution of a soluble silicate as a binder into said desired shape, said green mixture containing from 6 to 100 parts by weight of said aqueous solution for each 100 parts by weight of said particulate material, the amount of said aqueous solution being sufficient to form a porous, plastic mass when combined with said particulate material, said soluble silicate containing an alkali metal, ammonium, an ammonium complex, or mixtures thereof as a cation, and a silicate as the anion, the anion to cation mole ratio being between 1:1 and 4:1, said soluble silicate further containing from 47 to 70% water;
- (b) said green mixture being molded in a box having an air permeable face with an open area of at least 1.5%;
- and
- (c) subjecting said molded shape to a force drying period of not more than about two minutes, during which at least 30% of the water in said aqueous solution is evaporated and said molded shape is hardened to a tensile strength of at least 20 pounds per square inch.
In the manufacture of a desired shape by forming a green mixture of a particulate material containing a binder therefor, into a mold having the desired shape and thereafter hardening said green mixture, the improvement which comprises
- (a) using as a binder for said green mixture an aqueous solution of a soluble silicate containing an alkali metal, ammonium, an ammonium complex, or mixtures thereof, as a cation and a silicate as the anion, the anion to cation mole ratio being between 1:1 and 4:1, the amount of said aqueous solution being between 6 and 100 parts by weight for each 100 parts by weight of said particulate material;
- and
- (b) providing at least two air permeable faces in said mold, said air permeable faces having an open area of at least 1.5%;
- and
- (c) applying a differential pressure between said air permeable faces sufficient to force air therebetween at a rate of at least 30 standard cubic feet per minute per 100 grams of said green mixture and within two minutes to evaporate at least 30% of the water from said aqueous solution, to increase the solids content thereof to at least 54% and harden said molded shape to a tensile strength of at least 20 pounds per square inch.