US 4,225,680 A · Urea formaldehyde foam with low shrinkage

Abstract

This foaming system includes a foaming agent solution and a resin solution. The foaming agent includes the relative amounts of 15 to 30 parts by weight of a salt of an alkyl diphenyl oxide sulfonate, 10 to 25 parts of 85% phosphoric acid and 15 to 25 parts urea, all in an aqueous solution. The resin solution includes a resin prepared by reacting 1 to 2.4 mols of formaldehyde per 1 mol of urea, 6.5 to 500 mmols polyethylene glycol as foam charring agent, 0.3 to 1.2 mmols of calcium carbonate as uniform foam cell size agent, 3 to 310 mmols of dicyandiamide as foam hydrolysis resistance agent, 2 to 30 mmols of sodium bromide as foam aging agent, and sufficient water to make a 35 to 45% solution. In preparing the foam, one part by weight of the foaming agent solution of about 5% solids concentration is aerated and then 1.0 to 1.5 parts by weight of the resin solution is sprayed thereon to obtain foam with an average linear shrinkage of about 0.25%.

Claims11

Dependent claims

Foam with very low shrinkage which is prepared from mixing an aqueous foaming agent solution and an aqueous urea-formaldehyde solution, the foaming agent solution comprises the relative amounts, in parts by weight, of 15 to 30 parts of an anionic surfactant selected from salts of diphenyl oxide sulfonates and mixtures thereof, 10 to 25 parts of 85% phosphoric acid, and 15 to 25 parts of urea;

the resin solution comprises a condensation product of urea and formaldehyde in the ratio of 1.0 to 2.4 mols of formaldehyde per mol of urea;
from 6.5 to 500 mmols of a foaming charring agent selected from ethylene glycol and polyalkylene glycols containing from 2 to 8 carbon atoms in the alkylene moiety and having an average molecular weight no greater than 200, glycerine, pentaerythrytol, sugars and mixtures thereof;
from 0.3 to 1.2 mmols of a component to provide uniform cell size in the foam selected from water-soluble alkaline earth metal salts and mixtures thereof;
from 3 to 310 mmols of a foam hydrolysis resistance component selected from dicyandiamide, guanylurea, calcium cyanamide, guanidine derivatives, hexamethylene tetramine and mixtures thereof;
and from 2 to 30 mmols of a foam aging component selected from water-soluble alkali metal halogens and mixtures thereof.

2 more elements

Dependencies are inferred from the claim text.

Urea formaldehyde foam with low shrinkage

Life of this patent

Urea formaldehyde foam with low shrinkage

Life of this patent

Abstract

Claims11