Laser welding aluminum to copper
AssigneeGeneral Electric Company
InventorMarshall G. Jones
Life of this patent
Estimating the term…
Abstract
Copper and aluminum conductors are butt welded or corner welded by a two-part process involving heating and melting the Cu-Al interface with energy from a pulse laser and simultaneously generating a contact pressure. The laser wavelength is 1.06 micrometers or less and a single 8 millisecond pulse is used. Brittle intermetallics are found in the flash but the narrow fusion zone in the weld is substantially free of intermetallics. High conductivity aluminum is successfully welded to electrolytic tough pitch (ETP) copper wire.
Claims6
A method of welding an aluminum conductor to a copper conductor comprising the steps of:
- butting together the conductors with a contact pressure greater than 100 pounds per square inch and, while maintaining the contact pressure, delivering a single laser pulse to the aluminum-copper interface having a pulse width of approximately 8 milliseconds and a wavelength not exceeding 1.06 micrometers, said laser pulse having sufficient energy to heat and melt metal adjacent the interface and force molten material outwardly into a flash containing intermetallics while leaving a narrow fusion zone substantially free of intermetallics.
A method of butt and corner welding a high conductivity aluminum conductor to an electrolytic tough pitch (ETP) copper conductor comprising the steps of:
- butting together the conductors with a contact pressure of 100-350 pounds per square inch and then delivering to the copper-aluminum interface a laser pulse with a pulse width of approximately 8 milliseconds and sufficient energy to heat and melt both metals and force molten material outwardly into a flash containing intermetallics and leaving a narrow fusion zone substantially free of intermetallics, said laser pulse having a wavelength not exceeding 1.06 micrometers.
A method of butt welding a high conductivity aluminum conductor to an electrolytic tough pitch (ETP) copper conductor comprising the steps of:
- butting together unground ends of the conductors with a contact pressure of 100-350 psi and, while maintaining the contact pressure, delivering a single laser pulse to the aluminum-copper interface having a pulse width of approximately 8 milliseconds and a wavelength of 1.06 micrometers, said laser pulse having sufficient energy to heat and melt metal at the interface and force molten material outwardly into a flash containing intermetallics while leaving a narrow fusion zone substantially free of intermetallics.