US 4,223,434 AGranted

Method of manufacturing a niobium-aluminum-germanium superconductive material

AssigneeThe United States of America as represented by the United States Department of Energy

InventorsJohn L. Wang, Milton R. Pickus, Kent E. Douglas

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method for manufacturing flexible Nb.sub.3 (Al,Ge) multifilamentary superconductive material in which a sintered porous niobium compact is infiltrated with an aluminum-germanium alloy and thereafter deformed and heat treated in a series of steps at different successively higher temperatures preferably below 1000.degree. C. to produce filaments composed of Nb.sub.3 (Al,G3) within the compact. By avoiding temperatures in excess of 1000.degree. C. during the heat treatment, cladding material such as copper can be applied to facilitate a deformation step preceding the heat treatment and can remain in place through the heat treatment to also serve as a temperature stabilizer for supeconductive material produced. Further, these lower heat treatment temperatures favor formation of filaments with reduced grain size and, hence with more grain boundaries which in turn increase the current-carrying capacity of the superconductive material.

Claims10

Dependent claims

A method for manufacturing a flexible superconductive material containing interconnecting filaments of a Nb.sub.3 (Al, Ge) superconductive phase comprising the steps of:

a. forming a porous niobium compact having a network of interconnecting pores;
b. sintering the thus formed niobium compact;
c. infiltrating into the interconnecting pores of the sintered compact an aluminum-germanium alloy by passing the sintered compact through a molten bath of the alloy so that the alloy infiltrates into and substantially fills the pores of the sintered compact to form a composite;
d. deforming the composite to elongate infiltrant alloy so that the alloy extends as filaments through the composite;
e. first, heating the deformed composite to a temperature sufficient to cause the infiltrated alloy to react with niobium and separate into two phases, one, which is composed almost entirely of germanium and another, which is peripheral to the germanium phase and is composed basically of aluminum reacted with niobium;
f. second, heating the composite to a second higher temperature so that a germanium-rich germanium-aluminum-niobium phase is formed peripheral to the aluminum-niobium phase, and;
g. third, heating the composite to a third temperature higher than the second temperature such that aluminum diffuses through the germanium rich phase and forms a Nb.sub.3 (Al, Ge) superconductive phase peripheral to the germanium phase.

4 more elements