Method of producing finely divided polymer particles
AssigneeFuji Photo Film Co., Ltd.
InventorsKenji Naito, Keitaro Ohe, Nobuo Tsuji
Life of this patent
Estimating the term…
Abstract
One can obtain finely divided polymer particles by dissolving a polymer in a water immiscible volatile solvent which has a boiling point lower than that of water, then dispersing the solution into an aqueous medium, and removing the solvent from the dispersed oil phase droplets.
Claims13
A light-sensitive photographic silver halide material comprising a support, a light-sensitive silver halide emulsion layer and a top protective layer or a backing layer containing therein finely divided, spherically shaped, homogeneous, polymer material consisting essentially of 1 or more polymers which has a high degree of uniformity in shape and particle size, and having an average particle size of from 1 to 10 microns, said particles produced by a method which consists essentially of
- (a) forming a polymer solution by dissolving one or more polymers comprising at least 50 weight % of a monomer selected from the group consisting of styrene, o- and p-chlorostyrene, vinyl toluene, .alpha.-methylstyrene, acrylic esters, methacrylic esters, acrylonitrile, butadiene, isoprene and vinyl acetate in a halogenated aliphatic hydrocarbon solvent which is insoluble in or substantially immiscible with water, and which has a lower boiling point than water or which forms an azeotropic mixture with water having a lower boiling point than water,
- (b) separately dissolving gelatin, a gelatin derivative, casein or a protein compound which is an amphoteric polymeric electrolyte which forms a hydrophilic colloid in water as a dispersion stabilizer in water and an anionic surface active agent having a SO.sub.3 M group wherein M represents an alkali metal or ammonium, as a dispersion aid in water,
- (c) combining the two solutions of step (b) to form an aqueous medium,
- (d) dispersing said polymer solution in the aqueous medium in droplet form, the viscosities of the aqueous medium and of the polymer solution and the surface tension between the aqueous medium and the polymer solution being controlled, whereby the polymer solution is dispersed as oil droplets in the aqueous medium, and
- (e) then removing the solvent from each droplet, whereby the oil droplets are converted to solid particles having an average particle size of about 1 to 10 microns which particles will not change in shape or dimension after the conversion.
A method of manufacturing a spherically shaped, homogeneous, finely-divided material consisting essentially of one or more polymers which has a high degree of uniformity in shape and particle size, and average particle size of from 1 to 10 microns, which consists essentially of
- (a) forming a polymer solution by dissolving one or more polymers comprising at least 50 weight % of a monomer selected from the group consisting of styrene, o- and p-chlorostyrene, vinyl toluene, .alpha.-methylstyrene, acrylic esters, methacrylic esters, acrylonitrile, butadiene, isoprene and vinyl acetate in a halogenated aliphatic hydrocarbon solvent which is insoluble in or substantially immiscible with water, and which has a lower boiling point than water or which forms an azeotropic mixture with water having a lower boiling point than water,
- (b) separately dissolving gelatin, a gelatin derivative, casein or a protein compound which is an amphoteric polymeric electrolyte which forms a hydrophilic colloid in water as a dispersion stabilizer in water and an anionic surface active agent having a SO.sub.3 M group wherein M represents an alkali metal or ammonium, as a dispersion aid in water,
- (c) combining the two solutions of step (b) to form an aqueous medium,
- (d) dispersing said polymer solution in the aqueous medium in droplet form, the viscosities of the aqueous medium and of the polymer solution and the surface tension between the aqueous medium and the polymer solution being controlled whereby the polymer solution is dispersed as oil droplets in the aqueous medium, and
- (e) then removing the solvent from each droplet, whereby the oil droplets are converted to solid particles having an average particle size of about 1 to 10 microns which particles will not change in shape or dimension after the conversion.
Dependencies are inferred from the claim text.