Crosslinked chlorinated polyethylene foam

A crosslinked, soft, flexible closed-cell suspension chlorinated high density polyethylene foam derived from a chlorinated high density polyethylene having about 25 to about 48 percent chlorine and a flexural modulus of less than about 15,000 psi as determined by ASTM Test No. 790, Method 1, Procedure A, said foam having a cell size of from about 0.05 to about 2 mm, a density of from about 2.5 to about 50 pcf, a tensile strength of from about 30 to about 600 psi, and a tensile elongation of from about 200 to about 500 percent and a flexural modulus from about 500 to about 6,000 psi, said foam being prepared by a process comprising

• (a) preparing a foamable mixture consisting of the product obtained by mixing a high density suspension chlorinated polyethylene containing from about 25 to about 48 percent of chemically combined chlorine and having a flexural modulus at 25.degree. C. of less than about 15,000 psi as determined by ASTM Test No. 790, Method 1, Procedure A, with a thermally decomposable chemical foaming agent;
• (b) melt molding said foamable mixture at a temperature below that of the decomposition temperature of said chemical foaming agent, into a molded foamable article having a thickness of between about 0.025" to about 0.4";
• (c) subjecting said molded formable article while maintained at a temperature below the decomposition temperature of said foaming agent to an ionizing radiation of about 2.5 to about 7.5 mrad, for a period of time sufficient to impart crosslinking sufficient to enable said molded foamable article to retain its shape;
• and
• (d) contacting the crosslinked molded foamable article, in a substantially oxygen-free environment with a heat transfer medium maintained at a temperature between about 150.degree. C. and about 350.degree. C. for a period of time sufficient to form the desired flexible product.