Pre-treatment for molybdenum or molybdenum-rich alloy articles to be plated
AssigneeThe United States of America as represented by the United States Department of Energy
InventorRalph R. Wright
Life of this patent
Estimating the term…
Abstract
This invention is a method for etching a molybdenum or molybdenum-rich alloy surface to promote the formation of an adherent bond with a subsequently deposited metallic plating. In a typical application, the method is used as a pre-treatment for surfaces to be electrolessly plated with nickel. The pre-treatment comprises exposing the crystal boundaries of the surface by (a) anodizing the surface in acidic solution to form a continuous film of gray molybdenum oxide thereon and (b) removing the film.
Claims8
A pre-treatment for a surface which is to be provided with a metallic plating deposited from solution, said surface being a material selected from molybdenum and molybdenum-rich alloys, comprising:
- anodizing said surface in aqueous amino-trimethylenephosphonic acid solution to form thereon a continuous gray molybdenum oxide film, and
- removing said film.
A pre-treatment for a surface which is to be provided with a metallic plating deposited from solution, said surface being a material selected from the group consisting of molybdenum and molybdenum-rich alloys, comprising:
- electro-etching said surface in chromic acid-nitric acid solution to provide the same with a film-free matte finish,
- anodizing the electro-etched surface in an acidic medium to form thereon a continuous gray molybdenum oxide film, and
- removing said film.
A method for etching a metallic material to be provided with a metallic plating, said material being selected from the group consisting of molybdenum and molybdenum-rich alloys, said method comprising:
- electro-etching said material in chromic acid--nitric acid solution at a current density in the range of from about 0.5 to 1.5 amperes/in.sup.2 to provide the surface thereof with a matte finish,
- anodizing the resulting material to form a continuous gray molybdenum oxide film thereon, and
- removing said film.
A method for etching a metallic material to be provided with a metallic plating, said material being selected from the group consisting of molybdenum and molybdenum-rich alloys, said method comprising:
- electro-etching said material to provide the surface thereof with a matte finish,
- anodizing the resulting material in aqueous amino-trimethylene-phosphonic acid solution to form a continous gray molybdenum oxide film thereon, and
- removing said film.
In the method of electrolessly nickel plating a surface of a metallic material selected from the group consisting of molybdenum and molybdenum-rich alloys, said method including the steps of rendering said surface catalytic for the aqueous-bath reduction of nickel cations to metallic nickel and the corresponding oxidation of hypophosphite anions to phosphite anions and then electrolessly plating the resulting catalytic surface with nickel from an aqueous nickel cation--hypophosphite anion bath, the improvement comprising preceding said rendering step with the following sequence of operations:
- electro-etching said surface in chromic acid--nitric acid solution at a current density in the range of from about 0.5 to 1.5 amperes/in.sup.2 to provide it with a film-free matte finish, anodizing the electro-etched surface to form thereon a continuous gray oxide film, and
- removing said film.
Dependencies are inferred from the claim text.