Back to results
US 4,205,055 AGranted
Dual pore-structure artificial carbon and graphite
AssigneeLe Carbone Lorraine
InventorsJacques Maire, Jacques Fourre, Jean P. Gervais
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
AssigneeLe Carbone Lorraine
InventorsJacques Maire, Jacques Fourre, Jean P. Gervais
Estimating the term…
Dual pore-structured carbon and graphite consist essentially of a macroporous agglomeration of strongly bonded microporous grains of carbon or graphite the radii of the macropores therein being from substantially 10 to 350 .mu.m and those of the micropores from substantially 0.2 to 1.0 .mu.m, with the macropores being joined by intercommunicating channels which form a fluid permeable structure. Such carbon or graphite has a density of from 0.70 to 1.50 grams/cc., a permeability to gases of from 20 to 500 cm.sup.2 /sec/atmos and a porosity of from 30 to 50%. Such materials are produced by including in a mixture of tar or pitch and finely divided solid carbonaceous material in suitable proportions, a particulate eliminable non-carbon-forming material having a particle size of 10 to 350 .mu.m, which material is substantially insoluble in said mixture, in a proportion sufficient to secure the desired porosity, shaping and then heating the mixture to effect carbonization and/or graphitization thereof and, after the product has cooled, giving any appropriate after-treatment to eliminate any heat treated residue from said particulate material and leave the desired porous structure.
An artificial dual pore-structured carbon or graphite which is suitable for use as a catalyst substrate or an electrode material consisting essentially of a macro-porous agglomeration of strongly bonded microporous grains of carbon or graphite, the radius of the macropores being from substantially 10 to 350 .mu.m and that of the micropores being substantially 0.2 to 1.0 .mu.m, said macropores being joined by intercommunicating channels thus forming a fluid permeable structure, said carbon or graphite having a density of from 0.70 to 1.50 gms/cc., a permeability to gases of from 20 to 500 cm.sup.2 /sec/atmos, and a porosity of from 30 to 50%.
A process for the production of an artificial dual pore-structured carbon suitable for use as a catalyst substrate or an electrode material consisting essentially of a macroporous agglomeration of strongly bonded microporous grains of carbon which process comprises preparing an aggregate of (a) 15-35% by weight of tar or pitch and (b) 85-65% by weight of a finely divided carbonaceous material having a particle size up to 100 microns, intimately admixing the resulting aggregate with a particulate, eliminable, non-carbon forming material which material is substantially insoluble in said aggregate, shaping the resulting product is desired shape by compression or extrusion, heating the resulting shaped product to a carbonisation temperature for a time sufficient to carbonize the pitch content thereof, cooling the carbonized shaped material and, when a residue of said particulate material is present in the cooled carbonaceous product, treating said cooled product to remove said residue therefrom, said particulate eliminable material being used in the form of particles which will produce macropores having a radius of 10 to 350 .mu.m in the ultimate product and in such a proportion that the resulting artificial carbon will have a density of from 0.70 to 1.50, a permeability to gases of from 20 to 500 cm.sup.3 /sec/atmos and a porosity of 30 to 50%.
A process for the production of an artificial dual pore-structured graphite suitable for use as a catalyst substrate or an electrode material consisting essentially of a macroporous agglomeration of strongly bonded microporous grains of carbon which process comprises preparing an aggregate of (a) 15-35% by weight of tar or pitch and (b) 85-65% by weight of a finely divided carbonaceous material having a particle size up to 100 microns, intimately admixing the resulting aggregate with a particulate, eliminable, non-carbon forming material, which material is substantially insoluble in said aggregate, shaping the resulting product to desired shape by compression or extrusion, heating the resulting shaped product to a carbonising temperature for a time sufficient to carbonize the pitch content thereof, further heating the resulting carbonised product to a temperature of at least 2600.degree. C. for a time sufficient to graphitize the same, and when a residue of said particulate material is present in the cooled graphitized product, treating said graphitized product to remove said residue therefrom, said particulate eliminable material being used in the form of particles which will produce macropores having a radius of 10 to 350 .mu.m in the ultimate graphitized product and in such a proportion that the resulting artificial graphite will have a density of from 0.70 to 1.50, a permeability to gases of from 20 to 500 cm.sup.3 /sec/atmos and a porosity of 30 to 50%.
Dependencies are inferred from the claim text.