Process for preparing calcined gypsum and gypsum board
AssigneeUnited States Gypsum Company
InventorEugene E. O'Neill
Life of this patent
Estimating the term…
Abstract
A process for preparing calcined gypsum (stucco) which comprises treating a mass of calcined gypsum by adding, with thorough blending, small portions of water (about 1-10% by weight) to the calcined gypsum, allowing it to heal, and grinding the healed stucco to recapture the rate of strength development and the ultimate strength which are adversely affected by the water addition. The principal advantage provided by the addition of small portions of water is a reduction in water demand which is retained despite the grinding and optional drying of the healed stucco. If the treated calcined gypsum is not used shortly after the healing procedure, it should be dried to provide storage stability. The reduced water demand is particularly useful in gypsum board manufacture.
Claims21
An improved process for manufacturing gypsum board characterized by using a reduced amount of water to fluidize calcined gypsum in forming a gypsum slurry which is fed to a board making machine while maintaining the compressive strength of the dried gypsum board which comprises:
- (1) supplying calcined gypsum feed to be conveyed to a gypsum slurry mixer;
- (2) conveying the calcined gypsum feed to a blender;
- (3) blending a small amount of water with said calcined gypsum, said water ranging from about 1% to about 10% by weight of the calcined gypsum feed;
- (4) allowing the water treated calcined gypsum to heal;
- (5) grinding the healed calcined gypsum to increase the surface area of the healed gypsum particles, whereby the surface is reactivated to improve the rate of strength development and the ultimate strength of the gypsum board product;
- (6) feeding the healed and ground calcined gypsum to a gypsum slurry mixer;
- (7) adding additional water to the healed and ground calcined gypsum in the slurry mixer, said additional water being added in an amount sufficient to provide from about 50 to about 85 parts of water, including water added in the blender, per 100 parts of the calcined gypsum which results in a substantially reduced amount of water to be evaporated from the wet board;
- (8) mixing the healed and ground calcined gypsum and water in the slurry mixer to form a homogeneous slurry;
- (9) feeding the slurry to a gypsum board making machine to form a wet gypsum board;
- (10) passing the wet gypsum board to a kiln to dry the board;
- and
- (11) recovering dry gypsum board consisting essentially of calcium sulfate dihydrate.
In a process for manufacturing gypsum board of the type wherein a small amount of water is blended with the calcined gypsum feed and the water treated calcined gypsum is allowed to heal, the healed calcined gypsum is fed to the gypsum slurry mixer, additional water is added to the slurry mixer and the healed mixture of calcined gypsum and water is mixed in the slurry mixer to form a homogeneous slurry, the slurry is fed to a gypsum board making machine to form a wet gypsum board, and the wet gypsum board is dried in a kiln to recover dry gypsum board consisting essentially of calcium sulfate dihydrate;
- wherein the improvement comprises:
- grinding the healed calcined gypsum to increase the surface area of the healed gypsum particles, whereby the surface is reactivated to improve the rate of strength development and the ultimate strength of the gypsum board product.
An improved process for preparing calcined gypsum characterized by providing the calcined gypsum with a reduced water demand while maintaining its ability to develop full compressive strength in a cast gypsum product which comprises:
- (1) supplying calcined gypsum feed to be conveyed to a blender;
- (2) conveying the calcined gypsum feed to the blender;
- (3) blending a small amount of water with said calcined gypsum, said water ranging from about 1% to about 10% by weight of the calcined gypsum feed;
- (4) allowing the water treated calcined gypsum to heal;
- (5) drying the healed calcined gypsum by subjecting it to elevated temperatures;
- (6) grinding the dried, healed calcined gypsum to increase the surface area of the healed gypsum particles, whereby the surface is reactivated to improve the rate of strength development and the ultimate strength in a gypsum product;
- and
- (7) recovering a dried, healed calcined gypsum which is storage stable, has reduced water demand and is capable of developing substantially full compressive strength in a gypsum product.
In a process for manufacturing calcined gypsum of the type wherein calcined gypsum is fed to a blender, a small amount of water is blended with the calcined gypsum in the blender, and the water treated calcined gypsum is allowed to heal whereby the healed calcined gypsum has a reduced water demand;
- wherein the improvement comprises:
- drying the healed calcined gypsum;
- and subsequently grinding the dried, healed, calcined gyspum to increase the surface area of the healed gypsum particles, whereby the surface is reactivated to improve the rate of strength development and the ultimate strength in gypsum product.
Dependencies are inferred from the claim text.