Method of densifying metal oxides
AssigneeCorning Glass Works
InventorsPeter P. Bihuniak, Lewis H. Brandes, Donald L. Guile
Life of this patent
Estimating the term…
Abstract
A method of densifying a fumed metal oxide is disclosed wherein the metal oxide is converted to a flowable sol and then dried to form a fragmented solid which is calcined. The calcined oxide may be wet milled to provide a slip for casting articles such as fused silica crucibles used in melting silicon. The method also permits the production of very refractory fused glass compositions from fumed metal oxides at temperatures substantially below those required where a melting step is employed.
Claims3
A method for producing glassy granules of high silica glass (>70% by weight SiO.sub.2) containing at least one metal oxide from Groups III and IV of the Periodic Table selected from the group of Al.sub.2 O.sub.3, B.sub.2 O.sub.3, GeO.sub.2, HfO.sub.2, ZrO.sub.2, and TiO.sub.2 which consists of the steps:
- (a) a silica-producing component and said Group III and/or Group IV metal oxide-producing component are passed through a flame burner to form a composite fumed product of uniform composition;
- (b) said composite fumed product is mixed with a polar liquid to form a flowable sol containing up to 45% solids content;
- (c) said polar liquid is removed from said sol to produce a fragmented solid;
- and then
- (d) said fragmented solid is calcined within the temperature range of 1150.degree.-1500.degree. C. to produce glassy granules.