Method of fabricating an elliptical core single mode fiber
AssigneeInternational Telephone and Telegraph Corporation
InventorMokhtar S. Maklad
Life of this patent
Estimating the term…
Abstract
A method of fabricating a low loss single mode optical fiber having an elliptically shaped core comprising subjecting a multi-layered coated substrate having at least a barrier, cladding and core layer to partial collapse, first on one side and then on the other side, to produce an intermediate product having a substantially cross-sectional elliptical shape of at least the core layer. This is followed by collapsing the composite structure into a cylindrical shaped optical fiber preform having an elliptically shaped core portion which is then heated and drawn into a single mode optical fiber having an elliptically shaped core portion.
Claims6
A method of fabricating an optical fiber suitable for transmission of a single mode of injected light through a substantially elliptically shaped core portion, comprising the steps of:
- preparing a multi-layered coated tube having at least a substrate, cladding and core layers of glass;
- heating said coated tube along the length of one side to a temperature sufficient to cause partial collapse of said one side;
- heating along the length of the opposite side of said coated tube to a sufficient temperature to cause partial collapse of said opposite side of said coated tube;
- and
- collapsing said partially collapsed coated tube to form a substantially cylindrically shaped optical fiber preform having a substantially elliptically shaped core portion.
A method of fabricating a low loss single mode optical fiber having an elliptically shaped core comprising the steps of:
- selecting, cleaning, drying, and polishing a fused silica tube substrate;
- depositing a barrier layer of substantially pure silica on the bore of said tube, depositing a cladding layer on said barrier layer, and depositing a core layer on said cladding layer, each of said layers being formed by a modified chemical vapor deposition process while rotating said tube and subjecting said tube to a traversing hot zone which produces an amount of heat sufficient to cause each of the layer forming materials to react and to deposit each of said layers as glass;
- subjecting said coated tube to heat sufficient to cause partial collapse of said coated tube on only one side of said tube, at a same time while drawing a partial vacuum on the bore of said coated tube and traversing said hot zone to cause partial collapse of one side of said tube;
- subjecting the opposite side of said tube to said heat source to cause partial collapse of said opposite side followed by traversing said hot zone along said opposite side to cause uniform partial collapse of said tube;
- subjecting said partially collapsed tube to rotation and exposure to collapsing temperature, traversing said hot zone to collapse said partially collapsed tube into a solid optical fiber preform having an elliptically shaped core portion;
- and
- drawing said preform into an optical fiber having an elliptically shaped core suitable for transmission of polarized injected light through said core.