Torsion bar and method of forming the same
AssigneeFMC Corporation
InventorsGeorge L. Joseph, Charles A. Brolin
Life of this patent
Estimating the term…
Abstract
A method of forming a torsion bar wherein steel, preferably an alloy steel of medium carbon content, is formed in the desired size and shape and is through hardened for providing a desired core hardness. The case of the bar is then hardened for transforming austenite in the case into martensite causing the case to expand thereby inducing high compressive stresses near the surface with the compressive stress decreasing radially inward of the surface. The core of the bar is retained below lower transformation temperature for resisting expansion of the case thereby inducing hoop and axial compressive stresses and radial tensile stressed in the case. A torsion bar formed by the method of the present invention is also disclosed.
Claims10
A method of forming a torsion bar or the like having an outer case and a core from a steel alloy bar of the desired size and shape and with a medium carbon content, or from a steel bar having similar hardenability characteristics;
- comprising the steps of through hardening the bar to a predetermined hardness of about Rockwell C 30 to C 40, case hardening the bar for transforming austenite in the case into martensite which expands inducing a high compressive stress near the surface of the bar with the compressive stresses diminishing radially inward to the center of the bar, and retaining the core at a temperature below the transformation temperature for resisting expansion of both the case and the core and for inducing hoop and axial compressive stresses and radial tensile stresses in the case.
An induction hardened torsion bar comprising:
- an alloy steel bar having a body of circular cross section and hardenability characteristics the same as or similar to an alloy steel having a medium carbon content within the range of about 0.28% to 0.60%, said bar including an outer case and a core within the case, said case including a variable composition of martensite and austenite with a high percent of martensite being at the outer surface and diminishing to approximately 80% martensite at the interface between the case and the core, said case having an induced hardness at 0.01 inches below the surface of a minimum of Rockwell C 46 and a maximum of C 58 and being subjected to induced hoop and axial compressive stresses and radial tensile stresses, said core having a hardness within the range of about Rockwell C 30 to C 35.
An induction hardened torsion bar comprising;
- an alloy steel bar having a body of circular cross section and a medium carbon content within the range of about 0.28% to 0.60%, said bar including an outer case and a core with the case having a radial depth of between about 25% to 40% of the bar radius, said case including a variable composition of martensite and austenite with a high percent of the martensite being at the outer surface and diminishing to approximately 80% martensite at the interface between the case and the core, said case having an induced hardness at 0.005 inches below the surface of a minimum of Rockwell C 52 and a maximum of C 58 and being subjected to induced hoop and axial compressive stresses and radial tensile stresses, said core having a hardness within the range of about Rockwell C 30 to C 40.