AssigneeBoard of Regents, for and on behalf of the University of Florida
InventorsLarry L. Hench, Michael M. Walker
Estimating the term…
Compositions possessing a porous, high specific area, silica-rich surface, or capable of developing such a surface in vivo, form strong bonds with bone tissue. These compositions are thus excellent materials for dental and surgical implants, or the coatings thereof. Examples of such compositions include highly porous glasses and glass-ceramics comprising at least about 80 weight percent silicon dioxide, hardened inorganic cements such as Portland cement and known silicon dioxide-based biologically active glasses and glass-ceramics. Neither calcium, sodium nor phoshorus compounds are necessary ingredients. Cements which develop the above described surface characteristics in vivo form a strong bond with both bone and implant when used in the fixation of dental and surgical implants, especially those made or coated with a biologically active silicon dioxide-based glass or glass-ceramic.
A dental or surgical implant having a surface for bonding to the bone of a recipient, said bonding surface comprising a biologically compatible glass, glass-ceramic or ceramic material comprising at least about 80 weight percent silicon dioxide and having a specific surface area of at least about 80 square meters per gram, a porosity of from about 10 to about 50 volume percent, and an average pore diameter of from about 20 to about 300 Angstroms.
A dental or surgical implant having a surface for bonding to the bone of a recipient, said bonding surface comprising a biologically compatible inorganic material capable of developing a porous silica-rich surface layer having a specific surface area of at least about 80 square meters per gram within about ten days' exposure to aqueous tris(hydroxymethyl)aminomethane buffer at a pH of 7.2 and a temperature of 37.degree. C., said material being other than a silicon dioxide--based glass or glass-ceramic containing less than about 80 weight percent silicon dioxide.
In a process for the fixation of a dental or surgical implant to bone comprising placing a wet cement between the surfaces of bone and implant and allowing said cement to harden, the improvement which comprises using a biologically compatible inorganic cement which, in the hardened state, is capable of developing a porous silica-rich surface layer having a specific surface area of at least about 80 square meters per gram within about ten days' exposure to aqueous tris(hydroxymethyl)aminomethane buffer at a pH of 7.2 and a temperature of 37.degree. C.
Dependencies are inferred from the claim text.