US 4,169,932 AGranted

Method of producing poly-p-phenyleneterephthalamide or its copolymers

OwnerLev B. Sokolov, Valentin M. Savinov +1inventors

InventorsLev B. Sokolov, Valentin M. Savinov, Vyacheslav S. Petrukhin

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method of producing poly-p-phenyleneterephthalamide or its copolymers residing in that p-phenylenediamine or p-phenylenediamine and an aromatic diamine of the diphenyl series is/are disclosed in amide-salt solvents consisting of linear or cyclic N-alkyl-substituted amides of acids and of salts of alkaline or alkaline-earth metals soluble in said amides in amounts of 1-3 moles per mole of diamines; terephthalic acid dichloride or a mixture of terephthalic acid dichloride and aromatic acid dichloride of the diphenyl series are introduced into the solutions obtained at 0.degree.-20.degree. C. in amounts equimolar to those of the diamines, a reaction mixture being thus formed; tertiary amines are introduced into said reaction mixture in amounts 2-6 moles per mole of the initial diamines; the reaction mixture is stirred for 3-70 minutes and the end product is separated from the mass obtained. The method proposed herein is technologically simple and provides high-molecular polymeric products suitable for manufacturing heat-resistant, high-strength, and high-modulus fibres.

A process for producing a fiber forming poly-para-phenyleneterephthalamide or a copoly-para-phenyleneterephthalamide comprising the steps of:

(1) dissolving para-phenylenediamine or a mixture of 50 to 95 mol. percent of p-phenylenediamine with 50 to 5 mol. percent of an aromatic diamine of the diphenyl series selected from the group consisting of benzidine, 4,4'-diaminodiphenyl oxide, 4,4'-diaminodiphenyl sulfone, 4,4'-diaminobenzophenone, ortho-tolidine, ortho-dianisidine, in an amide-salt solvent in which the metal salt is used in an amount of between 1 and 3 mole per mole of the dissolved aromatic diamines and is selected from the group consisting of organic or inorganic alkali or alkaline earth metal salts soluble in the amide solvent and in which the amide solvent is selected from the group consisting of linear N-dialkyl-substituted carbamic acids, lower aliphatic acids and inner cyclic N-alkyl-substituted amides of aliphatic aminoacids, to obtain a solution thereof;
(2) adding to said solution with stirring at a temperature in the range of from about 0.degree. to +20.degree. C. terephthalic acid dichloride or a mixture of 50 to 95 molar percent of terephthalic acid dichloride with 50 to 5 molar percent of a dichloride of an aromatic diacid of the diphenyl series selected from the group consisting of diphenyl-4,4'-dicarboxylic acid dichloride, diphenyloxide-4,4'-dicarboxylic acid dichloride, benzophenone-4,4'-dicarboxylic acid dichloride in which said aromatic diacid dichloride is employed in equimolar amounts with said aromatic diamine, to obtain a homogeneous reaction mixture;
(3) adding to said reaction mixture, with stirring, a tertiary amine selected from the group consisting of .alpha.-picoline, .beta.-picoline, N,N-dimethylbenzylamine, N,N-dimethylaniline, quinoline, pyridine, triethylamine, N-methylmorpholine, in an amount of from 2 to 6 moles per mole of the starting aromatic diamines;
(4) stirring the resulting reaction mixture for a period of from 3 to 70 minutes to obtain poly-para-phenyleneterephthalamide, and (5) separating the resulting

1 more element