Solvent-free hot melt compositions for use as sealants, adhesives, caulking compounds or the like are produced by intimately blending elastomeric polymers with tackifying resins and plasticizers to obtain products having a hardness at room temperature of at least about 5 on the Shore A Durometer scale while being sufficiently soft at temperatures of about 150.degree. F. or higher to permit them to be easily extruded or otherwise applied. Adhesion promoters, lubricants, fillers and the like are preferably added to the composition to improve the properties thereof. The products are characterized by their stability over a wide range of temperatures, their resistance to oxidation and weathering, and their low moisture vapor transmission properties.
Claims10
Solvent-free, hot-melt compositions adapted to be extruded for use as sealants, adhesives, caulking compounds, expansion joints and the like consisting essentially of an unreacted mechanical mixture of 100 parts by weight of a polymerized elastomeric compound having a molecular weight above about 15,000 and selected from the group consisting of polyisobutylene, butadiene-styrene, styrene-butadiene-styrene polymers, styrene-isoprene polymers, chlorinated rubbers, acrylic rubber and mixtures thereof, with from about 1 to 400 parts by weight of tackifying resins selected from the group consisting of terpene resins, polyterpene resins, phenolic resins, hydrogenated rosin, hydrocarbon resins and mixtures thereof;
- from about 15 to 600 parts by weight of plasticizers selected from the group consisting of polybutenes, low molecular weight polyisobutylenes, phosphate esters, dibutyl phthalate, straight chain aliphatic acid esters, paraffin oils, coal tars, asphalts, chlorinated polyphenyl, chlorinated biphenyl and mixtures thereof;
- from about 0.5 to 60 parts by weight of adhesion promoter comprising the combination of an eopxy resin and an organic silane which is non-reactive with the epoxy resin, and from about 5 to 1000 parts by weight of an inert filler material;
- said composition being readily extrudable at temperatures above about 150.degree. F. while hardening upon cooling without undergoing chemical change, and having a hardness of about 5 to 95 on a Shore A Durometer at room temperature.
Solvent-free, hot-melt compositions adapted to be extruded for use as sealants, adhesives, caulking compounds, expansion joints and the like consisting essentially of an unreacted mechanical mixture of 100 parts by weight of elastomeric polyisobutylene having a molecular weight above about 15,000, with from about 1 to 400 parts by weight of tackifying resin selected from the group consisting of terpene resins, polyterpene resins, phenolic resins, hydrogenated rosin, hydrocarbon resins and mixtures thereof;
- from about 15 to 600 parts by weight of plasticizer selected from the group consisting of polybutenes, low molecular weight polyisobutylenes, phosphate esters, dibutyl phthalate, straight chain aliphatic acid esters, paraffin oils, coal tars, asphalts, chlorinated polyphenyl, chlorinated biphenyl, and mixtures thereof;
- from about 0.5 to 60 parts by weight of adhesion promoter comprising the combination of an epoxy resin having an epoxide equivalent of from about 150 to 3000 and an organic silane which is non-reactive with the epoxy resin;
- and from about 5 to 1000 parts by weight of an inert filler material;
- said composition being readily extrudable at temperatures above 150.degree. F. while hardening upon cooling without undergoing chemical change, and having a hardness of about 5 to 94 on a Shore A Durometer at room temperature.
A solvent-free hot melt composition adapted to be used as a sealant, caulking compound, expansion joint or the like consisting essentially of an unreacted mechanical mixture having approximately the following composition in parts by weight:
- ______________________________________ Polyisobutylene, having a molecular weight above about 15,000 100 Polyterpene resin 25 Calcium carbonate 50 Carbon black 10 Epoxy resin 20 Organic silane, which is non-reactive with epoxy resins 1 ______________________________________
- said composition being readily extrudable at temperatures above about 150.degree. F., while hardening upon cooling without undergoing chemical change, and having a hardness of about 5 to 94 on a Shore A Durometer at room temperature.
A solvent-free hot melt composition adapted to be used as a sealant, caulking compound, expansion joint or the like consisting essentially of an unreacted mechanical mixture having approximately the following composition in parts by weight:
- ______________________________________ Polyisobutylene, having a molecular weight above about 15,000 100 Calcium carbonate 50 Phenolic resin 50 Carbon black 10 Epoxy resin 20 Organic silane, which is non-reactive with epoxy resins 1 ______________________________________
- said composition being readily extrudable at temperatures above about 150.degree. F., while hardening upon cooling without undergoing chemical change and having a hardness of about 5 to 94 on a Shore A Durometer at room temperature.
A solvent-free hot melt composition adapted to be used as a sealant, caulking compound, expansion joint or the like consisting essentially of an unreacted mechanical mixture having approximately the following composition in parts by weight:
- ______________________________________ Polyisobutylene, having a molecular weight above about 15,000 100 Polyterpene 50 Calcium carbonate 50 Carbon black 10 Epoxy resin 20 Organic silane, which is non-reactive with epoxy resins 1 ______________________________________
- said composition being readily extrudable at temperatures above about 150.degree. F., while hardening upon cooling without undergoing chemical change, and having a hardness of about 5 to 94 on a Shore A Durometer at room temperature.