US 4,166,100 AGranted

Method of preparing granulated activated alumina

OwnerJury K. Vorobiev, Boris N. Badaev +15inventors

InventorsJury K. Vorobiev, Boris N. Badaev, Galina I. Ljubushko, Emmanuil A. Levitsky, Georgy K. Boreskov, Mikhail M. Andrushkevich, Bronislav A. Baum, Nikolai A. Pakhomov, Ljudmila G. Khomyakova, Alexandr E. Khramov, Nina A. Rodionova, Boris N. Isaev, Vladimir M. Knyazev, Ella M. Moroz, Vladimir N. Erofeev, Ivan P. Druzhinin, Rimma A. Shkrabina

Life of this patent

Estimating the term…

patentgrep

Loading patent…

Abstract

The method of preparing granulated activated alumina consists in that alumina trihydrate is decomposed by bringing it in contact with a bed of a solid heat carrier having the temperature of 350.degree. to 600.degree. C., the contact time being from 0.05 to 0.5 second, to obtain a product of decomposition in the form of amorphous aluminium hydroxide. Said decomposition product is mixed with water into a suspension having the concentration of 100-500 g/liter, calculating with reference to aluminium oxide, and hydrated at a temperature of 20.degree.-100.degree. C. and the pH of 5 to 12 for 0.5 to 10 hours. The hydrated decomposition product is then treated with an acid, that can form water-soluble basic salts of aluminium, at a temperature of 20.degree. to 150.degree. C., granulated, dried at a temperature of 20.degree. to 150.degree. C., and calcined at a temperature of 400.degree. to 600.degree. C. The granulated activated alumina can be used as an adsorbing material, as a catalyst, or a support for active components in chemical and petrochemical industry.

Claims6

Dependent claims

Method of preparing granulated activated alumina comprising the steps of:

decomposing alumina trihydrate by contacting it with a fluidized bed of a solid carrier having a temperature of from about 350.degree. C. to about 600.degree. C. for a contact time of from about 0.05 to about 0.5 seconds thereby to form a decomposition product composed of amorphous aluminum hydroxide;
mixing said decomposition product with water to form an aqueous suspension having a concentration of about 100 to 500 gram/liter calculated on the basis of aluminum oxide;
hydrating said decomposition product by adjusting said suspension of said decomposition product to a temperature of from about 20.degree. C. to about 100.degree. C. and a pH from about 5 to about 12 for about 0.5 to 10 hours;
treating the hydrated decomposition product with an acid that can form water soluble basic salts with aluminum at a temperature of about 20.degree. C. to about 150.degree. C.;
thereafter
granulating the acid treated decomposition product;
drying the granulated product at a temperature of from about 20.degree. C. to about 150.degree. C.;
and
calcinating the dryed granulated product at a temperature of about 400.degree. C. to about 600.degree. C.

6 more elements