US 4,164,416 A · Metal recovery process

Abstract

A process for the recovery of copper or lead from a sulfide ore concentrate containing the same. The ore concentrate, a carbonaceous material, an alkali metal carbonate and gaseous oxygen are introduced into a reaction zone to form a reaction mixture. The amount of carbonaceous material introduced is sufficient to reduce all of the copper or lead constituent of the sulfide ore to its elemental state in a single stage. A sufficient excess of carbonaceous material is provided to react with the oxygen and generate heat in situ to maintain the reaction zone at a temperature of from about 600.degree. to 1350.degree. C. thereby causing reduction of the metal sulfide to substantially pure copper or lead for recovery. The sulfur constituents of the ore react with the alkali metal carbonate to form sulfides. The other metal constituents of the ore are retained in the molten reaction mixture. In accordance with a preferred embodiment of the invention involving regeneration of the molten reaction mixture, at least a portion of the sulfide-containing molten reaction mixture is removed, quenched in an aqueous solution, and filtered to remove any insoluble reaction products. The aqueous filtrate is contacted with a CO.sub.2 -containing gas, preferably obtained from the reaction zone, to liberate the sulfur for recovery and reform carbonate for recycle to the reaction zone.

Claims11

Dependent claims

A process for the recovery of a metal selected from the group consisting of copper and lead from its respective sulfide ore, said process being performed under conditions resulting in substantially reduced emission of environmental pollutants, comprising:

(a) providing a reaction zone;
(b) introducing said sulfide ore containing from about 20 to 85 wt % of the selected metal, a carbonaceous material, an alkali metal carbonate and gaseous oxygen into said reaction zone to form a molten reaction mixture, said alkali metal carbonate and sulfide ore being introduced in amounts to provide a molar ratio of carbonate to metal sulfide of at least 1.2:1;
(c) said carbonaceous material being introduced in an amount sufficient to reduce substantially all of the selected metal sulfide to the elemental form of the metal and in a sufficient excess os that there is generated in situ substantially all the heat required to maintain the reaction zone at a selected temperature between 600.degree. and 1350.degree. C;
(d) maintaining the reaction zone at said selected temperature for a time sufficient for a reaction to occur in the mixture between the selected metal sulfide, the carbonaceous material and the alkali metal carbonate to form a desired amount of the selected metal in its elemental form in the molten state in a single stage, said molten metal settling to the bottom of the reaction zone;
and
(e) withdrawing the formed molten metal from the reaction zone as a flowable liquid substantially free of impurities.

3 more elements

(a) providing a reaction zone;
(b) introducing said sulfide ore containing from about 20 to 85 wt % of the selected metal, a carbonaceous material, an alkali metal carbonate and gaseous oxygen into said reaction zone to form a molten reaction mixture, said alkali metal carbonate and sulfide ore being introduced in amounts to provide a molar ratio of carbonate to metal sulfide of at least 1.2:1;
(c) said carbonaceous material being introduced in an amount sufficient to reduce substantially all of the selected metal sulfide to the elemental form of the metal and in a sufficient excess so that there is generated in situ substantially all the heat required to maintain the reaction zone at a selected temperature between 600.degree. and 1350.degree. C.;
(d) maintaining the reaction zone at said selected temperature for a time sufficient for a reaction to occur in the reaction mixture between the selected metal sulfide, the carbonaceous material and the alkali metal carbonate to form a desired amount of the selected metal in its elemental form in the molten state in a single stage, said molten metal settling to the bottom of the reaction zone;
(e) withdrawing the formed molten metal from the reaction zone as a flowable liquid subtantially free of impurities;
and
(f) withdrawing a side stream of the molten reaction mixture for regeneration of alkali metal sulfide contained therein to reform alkali metal carbonate for return to the reaction zone.