US 4,163,046 A · Recovery of selenium

Abstract

A hydrometallurgical process for treating copper refinery anode slimes containing selenium, lead and precious metals in which a selenium product of better than 99.7% purity can be produced and the final residue is suitable for smelting to produce anodes for silver refining.

Claims11

Dependent claims

A process for recovery of selenium from anode slimes containing selenium comprising:

(a) subjecting such slimes to a caustic oxidative leach to convert selenium values to the hexavalent form;
(b) neutralizing the product of the caustic leach with sulfuric acid to a pH of about 7 to about 9 with subsequent separation of the leach residue from the neutralized caustic leach solution;
(c) acidifying the separated neutralized leach solution with sufficient sulfuric acid to provide an acidified solution containing about 100 to about 200 grams per liter of sulfuric acid, and
(d) clarifying the resultant solution to obtain a further purified selenium-containing solution.

1 more element

A process for recovery of selenium from anode slimes containing selenium, tellurium, lead, copper and precious metal values, including silver, which comprises the successive steps of:

(a) subjecting the anode slimes to a caustic oxidative pressure leach as an aqueous slurry having a solids content of about 10% to about 30% in the presence of an alkali metal hydroxide in excess over the amount stoichiometrically necessary for extracting all the selenium values, lime in the amount about 2% to about 10% based on the weight of the anode slimes, and gaseous oxygen at an oxygen partial pressure of about 0.2 to about 1.5 MPa, at a temperature in the range of about 170.degree. C. to about 220.degree. C. for a period of about 3 to about 7 hours, to extract selenium in the hexavalent form;
(b) neutralizing the resultant product of the caustic leach with sulfuric acid to a pH of about 7 to about 9 and at a temperature of about 30.degree. C. to about 70.degree. C. to precipitate lead values;
(c) adding an aqueous-soluble sulfide to precipitate precious metal values;
(d) separating the residue of neutralization-sulfide treatment from the neutralized selenium-containing leach solution;
(e) acidifying the separated neutralized selenium-containing leach solution further with sulfuric acid at a temperature of about 30.degree. C. to about 60.degree. C., said added sulfuric acid being sufficient to provide a resultant acidified solution containing about 100 to 200 grams per liter of sulfuric acid;
and
(f) clarifying the resultant acidified solution to obtain a further purified selenium-containing solution.

4 more elements

In a process for the recovery of selenium or selenium from anode slimes containing selenium, tellurium, lead and precious metals, including silver, platinum and palladium values and containing silica, wherein the anode slimes are pre-treated for decopperization and/or the improvement comprising the steps of:

(a) subjecting said pre-treated anode slimes to a caustic oxidative pressure leach as an aqueous slurry having a solids content of about 10% to about 30% in the presence of an alkali metal hydroxide in excess over the amount stoichiometrically necessary for extracting all the selenium values, lime in the amount about 2% to about 10%, based on the weight of the anode slimes, and gaseous oxygen at an oxygen partial pressure of about 0.2 to about 1.5 MPa, at a temperature in the range of about 170.degree. C. to about 220.degree. C. for a period of about 3 to about 7 hours, to extract substantially all of the selenium and to precipitate substantially all of the tellurium;
(b) neutralizing the resultant product of the caustic leach with sulfuric acid to a pH of about 7 to about 9 and at a temperature of about 30.degree. C. to about 70.degree. C. to precipitate a preponderant part of the lead and silica;
(c) adding an aqueous-soluble sulfide to precipitate a major part of the palladium and platinum in the liquor;
(d) separating the product of neutralization into a selenium-containing leach solution and a tellurium-containing residue;
(e) acidifying the separated neutralized selenium-containing leach solution further with sulfuric acid at a temperature of about 30.degree. C. to about 60.degree. C., said added sulfuric acid being sufficient to provide a resultant acidified solution containing about 100 to 200 grams per liter of sulfuric acid;
and
(f) clarifying the resultant acidified solution to obtain a further purified selenium-containing solution;
(g) treating the further purified selenium-containing solution with sulfur dioxide at a temperature of about 90.degree. C. to about 100.degree. C. in the presence of sodium chloride in the amount of above 30 to about 70 grams per liter and ferrous sulfate in the amount of about 5 to about 20 grams per liter ferrous ion, the sulfuric dioxide being provided in at least sufficient amount to maximize precipitation of selenium values present in solution as elemental selenium.

5 more elements

Dependencies are inferred from the claim text.

Abstract

Claims11

Dependent claims

A process for recovery of selenium from anode slimes containing selenium comprising:

(a) subjecting such slimes to a caustic oxidative leach to convert selenium values to the hexavalent form;
(b) neutralizing the product of the caustic leach with sulfuric acid to a pH of about 7 to about 9 with subsequent separation of the leach residue from the neutralized caustic leach solution;
(c) acidifying the separated neutralized leach solution with sufficient sulfuric acid to provide an acidified solution containing about 100 to about 200 grams per liter of sulfuric acid, and
(d) clarifying the resultant solution to obtain a further purified selenium-containing solution.

1 more element

A process for recovery of selenium from anode slimes containing selenium, tellurium, lead, copper and precious metal values, including silver, which comprises the successive steps of:

(a) subjecting the anode slimes to a caustic oxidative pressure leach as an aqueous slurry having a solids content of about 10% to about 30% in the presence of an alkali metal hydroxide in excess over the amount stoichiometrically necessary for extracting all the selenium values, lime in the amount about 2% to about 10% based on the weight of the anode slimes, and gaseous oxygen at an oxygen partial pressure of about 0.2 to about 1.5 MPa, at a temperature in the range of about 170.degree. C. to about 220.degree. C. for a period of about 3 to about 7 hours, to extract selenium in the hexavalent form;
(b) neutralizing the resultant product of the caustic leach with sulfuric acid to a pH of about 7 to about 9 and at a temperature of about 30.degree. C. to about 70.degree. C. to precipitate lead values;
(c) adding an aqueous-soluble sulfide to precipitate precious metal values;
(d) separating the residue of neutralization-sulfide treatment from the neutralized selenium-containing leach solution;
(e) acidifying the separated neutralized selenium-containing leach solution further with sulfuric acid at a temperature of about 30.degree. C. to about 60.degree. C., said added sulfuric acid being sufficient to provide a resultant acidified solution containing about 100 to 200 grams per liter of sulfuric acid;
and
(f) clarifying the resultant acidified solution to obtain a further purified selenium-containing solution.

4 more elements

(a) subjecting said pre-treated anode slimes to a caustic oxidative pressure leach as an aqueous slurry having a solids content of about 10% to about 30% in the presence of an alkali metal hydroxide in excess over the amount stoichiometrically necessary for extracting all the selenium values, lime in the amount about 2% to about 10%, based on the weight of the anode slimes, and gaseous oxygen at an oxygen partial pressure of about 0.2 to about 1.5 MPa, at a temperature in the range of about 170.degree. C. to about 220.degree. C. for a period of about 3 to about 7 hours, to extract substantially all of the selenium and to precipitate substantially all of the tellurium;
(b) neutralizing the resultant product of the caustic leach with sulfuric acid to a pH of about 7 to about 9 and at a temperature of about 30.degree. C. to about 70.degree. C. to precipitate a preponderant part of the lead and silica;
(c) adding an aqueous-soluble sulfide to precipitate a major part of the palladium and platinum in the liquor;
(d) separating the product of neutralization into a selenium-containing leach solution and a tellurium-containing residue;
(e) acidifying the separated neutralized selenium-containing leach solution further with sulfuric acid at a temperature of about 30.degree. C. to about 60.degree. C., said added sulfuric acid being sufficient to provide a resultant acidified solution containing about 100 to 200 grams per liter of sulfuric acid;
and
(f) clarifying the resultant acidified solution to obtain a further purified selenium-containing solution;
(g) treating the further purified selenium-containing solution with sulfur dioxide at a temperature of about 90.degree. C. to about 100.degree. C. in the presence of sodium chloride in the amount of above 30 to about 70 grams per liter and ferrous sulfate in the amount of about 5 to about 20 grams per liter ferrous ion, the sulfuric dioxide being provided in at least sufficient amount to maximize precipitation of selenium values present in solution as elemental selenium.

5 more elements

Dependencies are inferred from the claim text.

Recovery of selenium

Life of this patent

Abstract

Claims11

Recovery of selenium

Life of this patent

Abstract

Claims11