US 4,158,738 AGranted
Process for the production of fiber-grade terephthalic acid
AssigneeE. I. Du Pont de Nemours and Company
InventorsLeon S. Scott, Roy W. Sommers
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
AssigneeE. I. Du Pont de Nemours and Company
InventorsLeon S. Scott, Roy W. Sommers
Estimating the term…
Process for the preparation of fiber-grade terephthalic acid by continuously oxidizing paraxylene while vaporizing a portion of the contents of the reactor. Fiber-grade terephthalic acid is produced by maintaining (1) a temperature of at least 210.degree. C., (2) a molecular oxygen content of the noncondensables in the vapor withdrawn from the reactor in the range 3.0-6.0%, (3) a water level of the contents of the oxidizer in the range 5.0-17.0%, (4) a mole ratio of sodium to cobalt plus manganese in the range 0.06-2.0 in the reactor, (5) a mole ratio of cobalt to manganese in the range 0.5-5.0 (6) an organic burn in the range 8.0-15.0 burn units and (7) a productivity in the range 0.45-1.45 pounds of terephthalic acid per minute per 100 pounds of reactor contents.
In a process for the preparation of fiber-grade terephthalic acid comprising oxidizing paraxylene with a molecular oxygen containing gas in a reactor in the presence of a catalyst consisting essentially of cobalt, manganese, sodium and bromine and a solvent comprising a lower monocarboxylic acid wherein (1) the oxidation is conducted in the liquid phase, (2) a portion of the contents of the reactor is continuously vaporized, withdrawn from the reactor and at least a portion thereof condensed and returned to the reactor and (3) the product is continuously withdrawn and subjected to treatment after oxidation and before recovery of the terephthalic acid, the improvement comprising maintaining a high productivity of fiber-grade terephthalic acid by maintaining (a) the temperature of the contents of the reactor at at least 210.degree. C., (b) the molecular oxygen content of the vapor withdrawn from the reactor in the range 3.0-6.0% by volume at least in part by controlling the molecular oxygen introduced into the reactor, (c) the water level of the contents of the reactor in the range 5.0-17% by weight based upon the weight of the liquid portion of the contents of the reactor by controlling the amount of condensed vapor returned to the reactor (d) the mole ratio of cobalt to manganese in the range 0.5-5.0 (e) the burn in the range 8-15 burn units and (f) the productivity of the reaction in the range 0.45-1.45 pounds of terephthalic acid per minute per one hundred pounds of reactor contents.
A process for oxidizing paraxylene to terephthalic acid in the liquid phase in an oxidation zone in using an acetic acid solvent and the presence of a catalyst consisting of species of cobalt, manganese, sodium and bromine which are soluble in said solvent which process comprises contacting said paraxylene with air, vaporizing, removing and condensing a portion of the solvent, returning a portion of the condensed solvent to the oxidation zone and continuously removing a slurry of terephthalic acid from said zone while maintaining the conditions in the following ranges
A process for the preparation of fiber-grade terephthalic acid comprising oxidizing paraxylene with a molecular oxygen containing gas in a reactor in the presence of a catalyst consisting essentially of cobalt, manganese, sodium and bromine and a solvent comprising a lower monocarboxylic acid wherein (1) the oxidation is conducted in the liquid phase, (2) a portion of the contents of the reactor is continuously vaporized, withdrawn from the reactor and at least a portion thereof condensed and returned to the reactor and (3) the product is continuously withdrawn and subjected to treatment after oxidation and before recovery of the terephthalic acid wherein the process variables are maintained in relationship according to the following formula ##EQU4## wherein Burn= 8.0-15