Lithium containing ion exchange strengthened glass
AssigneePPG Industries, Inc.
InventorDale W. Rinehart
Life of this patent
Estimating the term…
Abstract
Glasses having 59-62% by weight SiO.sub.2, 10-12% Na.sub.2 O, 4-5.5% Li.sub.2 O, 15-23% Al.sub.2 O.sub.3, and 2-5% ZrO.sub.2 have been found to be excellent for ion exchange strengthening below the strain point by exchanging the lithium ions with larger alkali metal ions such as sodium. Such glasses possess low melting temperatures, wide working ranges, and good chemical durability. The glasses are also free from corrosive volatile components, and sheets of such glasses resist devitrification when subjected to subsequent bending processes.
Claims7
A glass composition capable of being ion exchange strengthened below its strain point, consisting essentially of, by weight on the oxide basis:
- 59 to 63% -- SiO.sub.2
- 10 to 13% -- Na.sub.2 O
- 4 to 5.5% -- Li.sub.2 O
- 15 to 23% -- Al.sub.2 O.sub.3
- 2 to 5% -- ZrO.sub.2
- and 0 to 5% total of non-essential components selected from the group consisting of MgO, MnO, TiO.sub.2, Sb.sub.2 O.sub.3, As.sub.2 O.sub.3, K.sub.2 O, PbO, SO.sub.3, colorants, and mixtures thereof;
- wherein the sum of the weight percentages of Al.sub.2 O.sub.3 and ZrO.sub.2 is 19 to 25%, and the ratio of Na.sub.2 O to ZrO.sub.2 is from 2.2 to 5.5.
An ion exchange strengthened glass article having a surface portion in compression and an interior portion in tension;
- the interior portion consisting essentially of, by weight on the oxide basis:
- 59to 63% -- SiO.sub.2
- 10 to 13% -- Na.sub.2 O
- 4 to 5.5% -- Li.sub.2 O
- 15 to 23% -- Al.sub.2 O.sub.3
- 2 to 5% -- ZrO.sub.2
- and 0 to b 5% total of non-essential components selected from the group consisting of MgO, MnO, TiO.sub.2, Sb.sub.2 O.sub.3, As.sub.2 O.sub.3, K.sub.2 O, PbO, SO.sub.3, colorants, and mixtures thereof;
- wherein the sum of the weight percentages of Al.sub.2 O.sub.3 and ZrO.sub.2 is 19 to 25%, and the weight ratio of Na.sub.2 O to ZrO.sub.2 is from 2.2 to 5.5;
- the surface portion differing from the interior portion in a lower content of Li ions and a greater content of alkali metal ions larger than Li ions.