Welding back-up tape
AssigneeGeneral Dynamics Corporation
InventorsWilliam A. Roden, Glenn L. Criger
Life of this patent
Estimating the term…
Abstract
An improved back-up tape for use in fusion welding metal sheets and structures is disclosed. The tape comprises a rolled refractory fiber fabric partially flattened against an adhesive coated surface of a wider, heat resistant, strip. In use, the tape is pressed against the back side of a joint or other weld line to be welded with the adhesive bonding the tape along strips parallel to but slightly spaced from the weld line and the roll pressed against the joint. Fusion welding is conducted without the addition of any filler wire. A flat weld underbead, with no molten metal drop-through is produced, with no melting or other significant change in the tape. The tape is then stripped off and the welded structure is ready for use.
Claims9
A welding back-up tape comprising:
- an elongated narrow thin strip of flexible flat material;
- an adhesive coating on one surface of said strip;
- an elongated refractory fiber fabric sheet rolled about an axis parallel to the longer sides of said sheet;
- said roll having at least two fabric layers around the circumference of said roll and a hollow core;
- said roll being in bonding contact with said strip substantially along the centerline of said strip;
- whereby said roll and said strip may be pressed against a structure and held in place by said adhesive coating along the edges of said strip adjacent to said roll.
In a fusion welding system for butt welding aluminum structures comprising aluminum structures in close fitting contact along a weld line, a welding head on one side of said structures adapted to heat metal along said weld line to fusion temperature and a welding back-up assembly engaging the side of said structures opposite to said welding head and aligned with said weld line, the improvement wherein said welding back-up assembly comprises a strip of glass fiber fabric having an adhesive coating on one side, an elongated roll of glass fiber fabric, said roll partially flattened and bonded to said adhesive layer substantially along the centerline of said strip, said assembly pressed against said structures with said roll in contact with said weld line and said adhesive layer along the margins of said strip adjacent to said roll releasably bonding said assembly to said structures, said roll resisting significant degradation at the fusion temperature of aluminum.
A method for fabricating a welding back-up tape which comprises the steps of
- providing an elongated narrow strip of thin flat material;
- coating one surface of said strip with an adhesive layer;
- preparing a roll assembly by rolling an elongated refractory fiber fabric sheet about an axis parallel to the longer sheet edges until there are at least two fabric layers around the circumference of the roll;
- placing said roll assembly along the approximate centerline of said strip;
- partially flattening said roll assembly against said strip;
- said roll having a flattened width less than the width of said strip;
- and
- bonding said partially flattened roll to said strip by said adhesive.