Process for making refractory shapes
AssigneeLava Crucible Refractories Company
InventorsEldon D. Miller, Ryan F. Washburn
Life of this patent
Estimating the term…
Abstract
This application relates to a process for making ceramic shapes from nonplastic size graded ceramic materials comprising the formulation of a unique batch. The batch is processed in a water-cooled pug mill-extruder to prepare a deaired and densified column. The column is cut into constant volume billets. The billets are then pressed or reformed at low pressures into uniformly sized shapes which are thereafter dried and fired to develop a ceramic bond.
Claims4
A method of making a ceramic shape from a batch comprising nonplastic materials comprising raw clay wherein said raw clay is present in an amount of less than 5% comprising the steps for:
- A. preparing a batch comprising nonplastic size graded ceramic materials comprising less than 5% raw clay, 2 to 10%, by weight, volatilized silica;
- and 13 to 18 volume percent based on the entire batch, of organic binders, lubricants, and liquid vehicle;
- B. processing the batch in a pug mill-extruder to deair and extrude a continuous column, said pug mill-extruder having means for maintaining the temperature of the extrusion barrel of said extruder near room temperature thereby maintaining the surface of the column near room temperature while it is being extruded;
- C. cutting the column to form a billet;
- D. pressing the billet to form a shape;
- E. drying and firing to recover a ceramically bonded shape.
A method of making a ceramic shape from a batch comprising nonplastic materials comprising raw clay wherein said raw clay is present in an amount of less than 5% comprising the steps for:
- A. preparing a brickmaking batch comprising nonplastic size graded ceramic materials comprising less than 5% raw clay passing 8 mesh;
- 2 to 10% by weight volatilized silica;
- and 13 to 18 volume percent, based on the entire batch of organic binders and lubricants selected from the group consisting of dextrine, carboxymethyl cellulose, polyvinylalcohol, polyethylene oxide, and mixtures thereof, and water;
- B. processing the batch in a pug mill-extruder to deair and extrude a continuous column, said pug mill-extruder having means for maintaining the temperature of the extrusion barrel of said extruder near room temperature thereby maintaining the surface of the column near room temperature while it is being extruded;
- C. cutting the column to form a billet;
- D. pressing the billet to form a shape;
- E. drying and firing to recover a ceramically bonded shape.
Dependencies are inferred from the claim text.