Glass or ceramic-to-metal composites or seals involving iron base alloys
AssigneeOlin Corporation
InventorJames M. Popplewell
Life of this patent
Estimating the term…
Abstract
Glass or ceramic-to-metal composites or seals wherein the glass or ceramic is bonded to an iron base alloy consisting essentially of from 1-5% silicon and from 1-10% chromium, remainder iron. The alloy develops a thermal oxide film which consists essentially of chromium oxide and .alpha.Fe.sub.2 O.sub.3 which may comprise from 10 to 100% of the oxide film thickness on the metal. The invention also includes a process of bonding the glass or ceramic to the metal which eliminates the need of a prolonged heat treatment performed in a special atmosphere.
Claims5
A process for forming a glass or ceramic-to-metal composite or seal which comprises:
- preparing an iron base alloy component by providing a mixture comprising from 1-10% chromium, balance iron, and adding to said mixture from 1-5% silicon as based on the total resulting mixture thereof;
- oxidizing said iron base alloy component by heating in air at a temperature of up to 800.degree. C. for a maximum of three minutes to form on the surface of said component a thin, adherent oxide film consisting essentially of chromium oxide and .alpha.Fe.sub.2 O.sub.3 ;
- and
- placing a quantity of glass or ceramic metal on the surface of said oxidized iron base alloy component and heating the so-coated component at the sealing temperature of said glass or ceramic for a time sufficient to fuse said glass or ceramic to said iron base alloy component, wherein said composite may be characterized by a high degree of mismatch of coefficient of thermal expansion between said glass or ceramic and said iron base alloy component.
A process for forming a glass or ceramic-to-metal composite or seal which comprises:
- preparing an iron base alloy component by providing a mixture comprising from 1-10% chromium, balance iron, and adding to said mixture from 1-5% silicon as based on the total resulting mixture thereof;
- and placing a quantity of glass or ceramic material on the surface of said iron base alloy component and heating said component in air at the sealing temperature of said glass or ceramic for a time sufficient to fuse said glass or ceramic to said component while oxidizing said iron base alloy component to form a thin adherent oxide film consisting essentially of chromium oxide and .alpha.Fe.sub.2 O.sub.3, wherein said composite may be characterized by a high degree of mismatch of coefficient of thermal expansion between said glass or ceramic and said iron base alloy component.
Dependencies are inferred from the claim text.