US 4,147,758 A · Production of aluminum polyphosphate

Abstract

Aluminum polyphosphate is made. To this end, solid aluminum hydroxide and polyphosphoric acid which are used in proportions corresponding to an Al:P molar ratio of 1:2.5 to 1:3.5, are introduced separately from, but concurrently with, one another into a reaction zone kept at 150.degree. to 200.degree. C. A moist friable consistency of the starting materials is maintained in the reaction zone by continuously mixing, kneading and comminuting them over substantially the entire period during which they are introduced into the reaction zone. The reaction is continued until a dry sandy powder is formed; and the powder is annealed at 400.degree. to 600.degree. C. over a period sufficient to yield a product undergoing a 0.5 to 1% weight loss on ignition.

Claims5

Dependent claims

A process of producing long chain aluminium polyphosphates as defined in ASTM 13-266, which comprises step (A) of introducing into a reaction zone as starting materials aluminum hydroxide and polyphosphoric acid containing 75 to 85 weight % of P.sub.2 O.sub.5 in amounts corresponding to a molar ratio of Al:P of 1:2.5 to 1:3.5;

continuously mixing, kneading and comminuting the starting materials in the reaction zone and heating the resulting mixture at a temperature of 150.degree. to 200.degree. C. for as long as necessary to ensure conversion to a dry, sandy, pulverulent intermediate product;
and step (B) of dehydrating said intermediate product by annealing it at temperatures within the range 400.degree. to 600.degree. C. for a period sufficient to yield a final product undergoing 0.5 to 1% weight loss on ignition.

Dependencies are inferred from the claim text.

Production of aluminum polyphosphate

Life of this patent

Production of aluminum polyphosphate

Life of this patent

Abstract

Claims5