Method of treating ferruginous slags
AssigneeOsaka Iron & Steel Co., Ltd.
InventorsKiyoshi Takai, Naraharu Yamamoto, Seiichi Yamamoto
Life of this patent
Estimating the term…
Abstract
The disclosure is of a method of treating ferruginous metallurgical slags to lower basicity, stabilize their composition, reduce their melting point and stabilize the slag in regard to dusting and slaking. The stabilized slag is useful as an artificial sand or as an aggregated sand useful in the manufacture of concrete and like compositions.
Claims7
A method of improving a ferruginous metallurgical slag selected from the class of slags having a chemical composition including metallic iron, 35 to 59 parts by weight calcium oxide, 10 to 18 parts by weight silicon dioxide, 8 to 25 parts by weight total iron and a basicity (CaO/SiO.sub.2) of more than 1.65, which comprises;
- (a) providing said slag in a molten state;
- (b) adjusting the composition of the molten slag so as to include 2.0 to 8.0 parts by weight of total iron and 7.0 to 18.0 parts by weight Al.sub.2 O.sub.3 and a basicity (CaO/SiO.sub.2) of 1.3 - 1.65;
- (c) oxidizing metallic iron in the molten slag by blowing an oxygen containing gas into the adjusted molten slag;
- and
- (d) cooling the slag under conditions which yield a lump type slag, whereby the slag is stabilized against dusting and slaking.