Method for making structural foams with facing sheets
AssigneeExxon Research & Engineering Co.
InventorGlen E. W. Saidla
Life of this patent
Estimating the term…
Abstract
A method for forming a structural foam article having a cellular core, a high density integral skin with fiber reinforcement embedded therein, and exterior facing sheets so as to substantially avoid blistering of the facing sheets, is disclosed. The foam article is prepared by foaming an expandable resin composition between the fiber reinforcing material and facing sheets. The resin has a predetermined viscosity which is a direct function of the porosity of the reinforcing material and an indirect function of the foam initiation time.
Claims12
In forming a fiber-reinforced structural foam having an exterior layer of a substantially nonporous film material on at least one surface thereof and adherent to said foam by foaming a foamable resin composition in place in a mold first lined with an exterior layer of said film material and next with a first layer of fiber-reinforcing sheet material whereby after the resin composition foams the resulting foam is bonded to the facing sheet without adhesive, the improvement consisting essentially of:
- charging in the mold on said fiber-reinforcing sheet material a foamable resin composition for foaming therein, said resin composition being charged in an amount sufficient to fill the mold on foaming, and said resin composition having a viscosity prior to foaming such that under the conditions in which the resin composition is charged into the mold the resin would not flow by gravity through the openings between the fibers in the fiber-reinforcing material and form beads on the underside thereof in a time shorter than the foam initiation time;
- and allowing said resin composition to foam in place and completely fill the mold whereby a fiber-reinforced structural foam having a facing sheet on at least one surface is obtained.
A method of forming a fiber-reinforced structural foam consisting essentially of:
- (a) placing a sheet of polymeric film selected from acrylic film and polyvinylfluoride film in a mold and then;
- (b) placing a sheet of fiberglass reinforcing sheet material in the mold on top of the facing material;
- (c) placing a polyurethane foamable resin composition in the mold on said fiberglass reinforcing sheet material for foaming in place therein, said foamable resin composition being sufficiently viscous prior to foaming such that the drip time of the resin is greater than the foam initiation time;
- and
- (d) allowing the resin to foam thereby forming a fiber-reinforced structural foam article having a facing sheet which is blister free.
A method of forming a structural foam board having a cellular foam core and integral skins of relatively high density foam on two major surfaces of the board, said integral skins having a fiber-reinforcing sheet material embedded therein, said foam board having facing sheet material on the exterior of the two major surfaces, said method consisting essentially of:
- foaming in place in said mold an expandable polyurethane resin composition between the two layers of said fiber-reinforcing sheet material and the facing sheet material, said fiber-reinforcing sheet material being fiberglass sheet material and said facing sheet material being a substantially nonporous polymeric film material which is capable of adhering to said polyurethane resin composition, said resin composition having a viscosity prior to foaming and under the conditions in which it is loaded into the mold such that said resin would not flow by gravity through openings between the fibers in the fiber-reinforcing sheet material and forming beads on the underside thereof and in a time less than the foam initiation time.
A method of forming a structural foam board consisting essentially of:
- (a) placing a sheet of plastic film sheet facing material in a mold, said plastic film sheet material being selected from acrylic and polyvinyl films;
- (b) placing a sheet of woven fiberglass roving in the mold on top of the facing sheet material, said fiber-reinforcing sheet material being a style 30 woven glass roving with from about 3 to about 8 yarns in the warp and from about 3 to about 8 yarns in the woof;
- (c) placing an expandable resin composition for foaming in place in the mold, said resin being placed on top of the reinforcing woven fiberglass roving in an amount sufficient to fill the mold upon foaming, said resin composition being sufficiently viscous prior to foaming and under the conditions in which the resin composition in loaded into the mold such that foam initiation time is less than the time the resin can flow by gravity through the woven roving and form beads of resin on the underside thereof;
- (d) covering the resin composition with a second layer of woven fiberglass roving and then a second layer of plastic film sheet facing material;
- (e) placing a platen over the mold;
- and
- (f) allowing the resin to foam thereby forming a fiber-reinforced foam board having facing sheets which are blister free.
The method of claim 14 wherein said fiberglass roving has openings between the fibers thereof which is graded with the openings increasing from the center area of the woven fiberglass to its outer extremities and wherein the resin is placed so as to substantially coincide with the center area of the woven fiberglass.
In the method of forming a structural polyurethane foam board by foaming an expandable polyurethane resin composition between sheets of woven fiberglass roving and polyvinyl fluoride plastic film sheet material exterior the woven fiberglass roving, the improvement consisting essentially of:
- charging an expandable polyurethane resin composition between the sheets of woven fiberglass roving in a mold in an amount sufficient to completely fill the mold upon foaming, said woven fiberglass roving having two side panel areas and a center panel area therebetween, the openings between the fibers of the roving in the side panel areas being greater than the openings between the fibers in the roving in the center area, said resin being placed between the sheets in the center area, said resin composition prior to foaming having a drip time relative to the center area of woven fiberglass roving which is greater than the foam initiation time of the resin composition;
- and allowing the resin to foam.