US 4,117,077 AGranted

Process for alunite treatment

OwnerGakif Zakirovich Nasyrov, Evgenia Ivanovna Zemlyanskaya +1inventors

InventorsGakif Zakirovich Nasyrov, Evgenia Ivanovna Zemlyanskaya, Izabella Vladislavovna Ravdonikas

Life of this patent

Estimating the term…

Loading patent…

Abstract

A process for alunite ore treatment which comprises roasting alunite in the presence of oxygen at a temperature of from 580.degree. to 620.degree. C. for 1 to 3 hours, decomposing the roasted alunite by exposure to reducing agents at a temperature of from 580.degree. to 620.degree. C., subjecting the reduced alunite to hydrochemical treatment by use of a sodium hydroxide solution of concentration from 100 to 150 g/lit in terms of Na.sub.2 O, decomposing the resultant aluminate liquor, with the aluminum hydroxide component precipitating out, and finally, washing and baking the aluminum hydroxide precipitate to obtain same as an end product. The invention provides a comprehensive method of treatment of alunite ores the associated rock whereof comprises silica in the form of opal and chalcedony earlier believed to be refractory to comprehensive treatment by alkaline methods.

Claims7

Dependent claims

A process for the treatment of alunite ore containing silicon oxides in the form of opal and chalcedony which comprises:

(a) roasting said alunite ore in the presence of oxygen at a temperature of from 580.degree. to 620.degree. C. for 1 to 3 hours;
(b) decomposing the roasted alunite ore in the presence of a reducing agent at a temperature of from 580.degree. to 620.degree. C. for 40 to 60 minutes, to form a reduced alunite ore;
(c) leaching the reduced alunite ore at a temperature of from 45.degree. to 85.degree. C. by treatment with a solution of sodium hydroxide having a concentration of 100 to 150 grams per liter in terms of Na.sub.2 O, to extract aluminum oxide and a mixture of potassium and sodium sulfates into solution, and to form a residue which is separated from said solution;
(d) evaporating said solution to concentrate the sodium hydroxide to 200 to 220 grams per liter in terms of Na.sub.2 O, thereby precipitating the potassium and sodium sulfates, and separating said mixed surface precipitate;
(e) diluting the aluminum oxide solution to a sodium hydroxide concentration of from 120 to 150 grams per liter in terms of Na.sub.2 O;
(f) precipitating aluminum hydroxide from the aluminum oxide solution by seeding said solution under agitation with aluminum hydroxide;
and
(g) separating the aluminum hydroxide.

5 more elements

Dependencies are inferred from the claim text.