Heat treated superalloy single crystal article and process
AssigneeUnited Technologies Corporation
InventorsMaurice L. Gell, David N. Duhl
Life of this patent
Estimating the term…
Abstract
Nickel base superalloy single crystal articles formed from an alloy family and heat treated are described as is the process employed. The articles are substantially free from cobalt and the grain boundary strengtheners such as carbon, boron, and zirconium. The heat treatment process homogenizes the microstructure, and refines the gamma prime morphology.
Claims7
A single crystal nickel base superalloy article free from intentional additions of cobalt, carbon, boron, and zirconium, consisting essentially of from about 5 to about 18% chromium, at least 5% of an element chosen from the group consisting of from 2 to 8% aluminum and from 1 to 5% titanium and mixtures thereof;
- at least 5% of an element chosen from the group consisting of up to 10% molybdenum, up to 15% tungsten, up to 12% tantalum, up to 3% columbium, up to 3.5% hafnium, up to 7% rhenium, and mixtures thereof;
- balance essentially nickel;
- said single crystal article having a homogeneous microstructure which contains gamma prime particles having a size of less than 0.5 microns, and said microstructure being free of MC type carbides, and TCP phases.
A method for producing nickel base superalloy single crystal articles which have a homogeneous microstructure and in which the gamma prime phase presents a refined morphology, including the steps of:
- a. providing a mass of nickel base superalloy material which is free from intentional additions of a cobalt, carbon, boron, and zirconium;
- and which consists essentially of from about 5 to 18% chromium;
- at least 5% of an element chosen from the group consisting of from 2 to 8% aluminum and from 1 to 5% titanium and mixture thereof;
- at least 5% of an element chosen from the group consisting of up to 10% molybdenum, up to 15% tungsten, up to 12% tantalum, up to 3% columbium, up to 3.5% hafnium, up to 7% rhenium, and mixtures thereof;
- balance essentially nickel,
- b. melting the nickel base superalloy and solidifying the alloy under conditions of unidirectional heat flow so as to produce a single crystal article having a microstructure which consists essentially of gamma prime particles in a gamma prime matrix, with the gamma prime particles having a particle size of about 1.5 microns, said article having an incipient melting temperature, in excess of about 2300.degree. F., as a result of the absence of carbon, boron and zirconium, and a gamma prime solvus temperature, which is less than the incipient melting temperature, said microstructure being free of MC type carbides as a result of the absence of carbon and free from TCP phases, as a result of the absence of cobalt,
- c. heating the article to a temperature greater than the gamma prime solvus temperature and less than the incipient melting temperature for a period of time sufficient to dissolve substantially all of the gamma prime phase into solid solution while simultaneously homogenizing the microstructure,
- d. heating the article at a temperature below the gamma prime solvus for a period of time sufficient to reprecipitate the gamma prime phase in refined form,
- whereby the reprecipitated gamma prime phase has a particle size of less than about 0.5 microns and the heat treated single crystal article has a temperature advantage of at least 30.degree. F. over non-heat treated articles.
Dependencies are inferred from the claim text.