Method for making a monolithic ceramic capacitor employing a non-reducing dielectric ceramic composition
AssigneeMurata Manufacturing Co., Ltd.
InventorsYukio Sakabe, Hiroshi Seno
Life of this patent
Estimating the term…
Abstract
Non-reducing dielectric ceramic compositions comprise solid solutions which are represented by the compositional formula: {(Ba.sub.1-x Ca.sub.x)O}.sub.m .multidot.(Ti.sub.1-y Zr.sub.y)O.sub.2 wherein m, x and y have the following values: 1.005 .ltoreq. m .ltoreq. 1.03 0.02 .ltoreq. x .ltoreq. 0.22 O < y .ltoreq. 0.20 The compositions possess high permittivity and small dielectric loss and maintain high insulation resistance even if fired in reducing atmospheres, thus making it possible to manufacture inexpensive but high reliable monolithic or multi-layer ceramic capacitors.
Claims3
A method for making a monolithic ceramic capacitor with internal electrodes made of base metal or alloy of the group consisting of nickel, iron, cobalt and alloys thereof, the method comprising the steps of preparing a plurality of dielectric green sheets with a dielectric ceramic composition, forming an internal electrode on each green sheet, stacking and pressing the resultant green sheets to form a monolithic multilayer unit, and providing terminations for the resultant monolithic unit, the terminations being electrically connected to the internal electrodes of the monolithic unit, wherein the improvement comprises mixing and presintering raw materials in such compositional proportions to produce said dielectric ceramic composition having the formula
- {(Ba.sub.1-x Ca.sub.x)O}.sub.m.(Ti.sub.1-y Zr.sub.y)O.sub.2
- wherein
- 1.005 .ltoreq. m .ltoreq. 1.03
- 0.02 .ltoreq. x .ltoreq. 0.22
- 0 <
- y .ltoreq. 0.20,
- and the firing is effected in a reducing atmosphere containing hydrogen.
Dependencies are inferred from the claim text.