Production of porous sintered PTFE products
AssigneeW. L. Gore & Associates, Inc.
InventorEtsuo Yamazaki
Life of this patent
Estimating the term…
Abstract
The present invention provides porous polytetrafluoroethylene ("PTFE") products having fine pores and high porosity, the pore diameter being less than about 1,500A, generally ranging from about 100A to 1,000A. The process for the manufacture of these products comprises: (a) shaping of a lubricated PTFE mixture, by extrusion and/or rolling; (b) a first stretching of the shaped mass while in an unsintered state; (c) free sintering of the stretched mass at a temperature above 327.degree. C; and (d) a second stretching of the sintered mass. These porous PTFE products are suitable for use as gas separators, diaphragms, filters, and other applications.
Claims6
A process for producing a porous product of sintered polytetrafluoroethylene, having a pore size of less than 2000A, which comprises the following steps performed in sequence:
- (a) shaping an unsintered polytetrafluoroethylene mixture, containing a liquid lubricant, by extrusion, below the crystalline melt point of the polytetrafluoroethylene, to form a shaped extrudate;
- (b) a first stretching of said shaped extrudate in at least one direction at a temperature below about 327.degree. C;
- (c) free sintering by heating said stretched shaped extrudate to a temperature above 327.degree. C, said stretched shaped article being unrestrained and allowed to shrink to almost the same size it had been before stretching;
- and
- (d) a second stretching of said sintered, stretched, shaped extrudate at a temperature below the crystalline melt point at a speed in the range of about 1 .times. 10.sup.2 to about 2 .times. 10.sup.6 mm/min.
Dependencies are inferred from the claim text.