Process for manufacture of macroporous microspheroids
AssigneeE. I. Du Pont de Nemours and Company
InventorsRalph K. Iler, Joseph J. Kirkland
Life of this patent
Estimating the term…
Abstract
Disclosed herein is a powder of discrete, macroporous, microspheroids, each having an average diameter in the range of 2 to 50 microns and each composed of a plurality of large colloidal particles joined and cemented together at their points of contact by 1 to 10% by weight of non-porous, amorphous silica. These microspheroids have a high degree of mechanical stability and a surface area between about 80 and 110% of that of the large colloidal particles. Also disclosed is a process for the manufacture of this powder.
Claims4
A process of producing a powder of discrete, macroporous, microspheroids comprising the steps of:
- (a) forming a powder of microspheroids, each having an average diameter in the range of about 2 to about 50 microns, each microspheroid being a coherent aggregate of:
- (1) a plurality of large colloidal particles having an average diameter in the range of about 0.1 to about 1.0 micron and each having a surface of silica and a core of material selected from the group consisting of silica and acid-insoluble refractory metal oxides, and
- (2) a plurality of small colloidal silica particles having an average diameter of about 1.0 to about 10.0 nanometers, the average diameter of said small colloidal particles being less than or equal to about one-tenth the average diameter of said large colloidal particles, and
- (b) heating the microspheroids so formed to a temperature in the range of about 650.degree. to about 1050.degree. C. until the small colloidal particles have sintered to each other and to the large colloidal particles forming a nonporous silica coating joining and cementing together the large colloidal particles.
Dependencies are inferred from the claim text.