Porcelain fused to metal crown

A porcelain fused to metal crown having a composite structure comprising layers of a bonding agent, a mixture of a bonding agent and ceramics, ceramics, and optionally a mixture of a ceramics and a porcelain, which are thermally sprayed around the metal crown, and a layer of fused porcelain formed on the above layers.

A porcelain fused to metal crown having a composite structure comprising layers of a bonding agent, a mixture of a bonding agent and ceramics or ceramics and a mixture of ceramics and a porcelain, and a layer of fused porcelain formed on the above layers.

A process for producing a porcelain fused to metal crown, which comprises producing a metal crown by casting a dental casting alloy, thermally spraying thereon a bonding agent and ceramics to form layers of the bonding agent and the ceramics, and fusing thereon a porcelain to form a layer of fused porcelain.

A process for producing a porcelain fused to metal crown, which comprises producing a metal crown by casting a dental casting alloy, thermally spraying thereon a bonding agent, a mixture of a bonding agent and ceramics, and ceramics, and optionally a mixture of ceramics and porcelain, in order, to form layers thereof, and fusing thereon a porcelain to form a layer of fused porcelain.

A process for producing a porcelain fused to metal crown, which comprises producing a metal crown by casting a dental casting alloy, thermally spraying thereon a bonding agent, a mixture of a bonding agent and ceramics or ceramics and a mixture of a ceramics and a porcelain, in order, to form layers thereof, and fusing thereon a porcelain to form a layer of fused porcelain.

A porcelain fused to a metal crown having a composite structure comprising layers of a bonding agent, a mixture of a bonding agent and zirconium oxide ceramics and a layer of a ceramic mixture of 10 to 100% by weight of zirconium oxide and 90 to 0% by weight of aluminum oxide, and optionally a mixture of a ceramic and porcelain, which are thermally sprayed on the metal crown, and a layer of fused porcelain formed on the above layers.

A porcelain fused to a metal crown having a composite structure comprising layers of a bonding agent, a mixture of a bonding agent and a ceramic or zirconium oxide ceramic and a mixtuee of zirconium oxide and aluminum oxide ceramics with a porcelain, and a layer of fused porcelain formed on the above layers.

A porcelain fused metallic tooth crown comprising a metallic tooth crown base made of a dental casting alloy, a thermally sprayed layer of a bonding agent selected from the group consisting of molybdenum, tantalum, niobium, a nickel-chromium-aluminum powdery mixture, and a nickel-aluminum powdery mixture which is formed around the metallic tooth crown base, a thermally sprayed layer of ceramics selected from the group consisting of aluminum oxide, zirconium oxide, titanium oxide and a mixture thereof which is formed on said layer of a bonding agent, and a surface layer of fused porcelain.

A porcelain fused metallic tooth crown comprising a metallic tooth crown base made of a dental casting alloy, a thermally sprayed layer of a bonding agent formed around the metallic tooth crown base, a thermally sprayed layer of a mixture of a bonding agent, a thermally sprayed layer of ceramics formed on the layer of a mixture of a bonding agent and ceramics, a surface layer of fused porcelain, and optionally a thermally sprayed layer of ceramics and porcelain which may exist between the layer of ceramics and the sueface layer of fused porcelain, said bonding agent being selected from the group consisting of molybdenum, tantalum, niobium, a nickel-chormium-aluminum powdery mixture and a nickel-aluminum powdery mixture, and said ceramics selected from the group consisting of aluminum oxide, zirconium oxide, titanium oxide, and a mixture thereof.

A porcelain-fused metallic tooth crown comprising a metallic tooth crown base made of a dental caating alloy, a thermally sprayed layer of a bonding agent formed around the metallic tooth crown base, a thermally sprayed layer of a mixture of a bonding agent and ceramics formed on the layer of a bonding agent, a thermally sprayed layer of ceramics formed on the layer of a bonding agent and ceramics, a thermally sprayed layer of a mixture of ceramics and porcelain formed on the layer of ceramics, and a surface layer of fused porcelain, said bonding agent being selected from the group consisting of molybdenum, tantalum, niobium, a nickel-chromium-aluminum powdery mixture, and a nickel-aluminum powdery mixture, and said ceramics selected from the group consisting of aluminum oxide, zirconium oxide, titanium oxide and a mixture thereof.