US 4,102,664 AGranted

Method for making glass articles with defect-free surfaces

AssigneeCorning Glass Works

InventorWilliam H. Dumbaugh, Jr.

Life of this patent

Estimating the term…

Loading patent…

Abstract

This invention relates to a method for forming glass articles having essentially defect-free surfaces which can be equivalent in smoothness to that achieved in a polishing operation, and which can demonstrate mechanical strength superior to that exhibited by glass articles produced via conventional glass-forming techniques.The method contemplates melting two different glass compositions, one of which is highly soluble in a given solvent and the second of which is relatively insoluble in the same solvent; the molten glasses are simultaneously brought together while in the fluid state to form a laminated glass body wherein the insoluble glass is essentially completely enveloped within the soluble glass; the laminae are fused together at a temperature where the melts are in fluid form to provide an interface therebetween which is free from defects; the laminated article is cooled; and the soluble outer glass layer is dissolved away in an appropriate solvent. An exchange of ions takes place at the interface between the insoluble glass and the soluble outer glass layer.

Claims4

Dependent claims

A method for forming strengthened glass articles having surfaces which are essentially defect free and equivalent in smoothness to polished surfaces which comprises the steps:

(a) two glass-forming batches of different compositions are melted, one batch for a glass which is highly soluble in a given solvent and the second for a glass which is relatively insoluble in the same solvent;
(b) the molten batches are simultaneously brought together while in the fluid state, that is, having viscosities no greater than about 250,000 poises, to form a laminated glass body wherein the insoluble glass is essentially completely enclosed within the soluble glass;
(c) the laminae are fused together at a temperature where the melts are in fluid form to provide an interface therebetween which is defect free and to cause an exchange of ions to take place at said interface between said insoluble glass and said soluble glass, the composition of the soluble glass being selected such that there is essentially no composition gradient at said interface but the migratable ions thereof enhance the chemical durability of the insoluble glass and cause the production of a surface layer on the insoluble glass having a coefficient of thermal expansion lower than that of the insoluble glass, and the composition of the insoluble glass being selected such that the migratable ions thereof enhance the solubility of the soluble glass;
(d) the laminated article is cooled;
and then
(e) the soluble glass layer is dissolved away in a solvent wherein it is at least 10 times more soluble than the insoluble glass.

3 more elements

Dependencies are inferred from the claim text.