Barium oxide coated zirconia particle for use in an oxygen extractor
AssigneeThe Bendix Corporation
InventorsPeter Hing-Shya Tsang, Richard W. Hradek, James Daniel Bode
Life of this patent
Estimating the term…
Abstract
A process of manufacturing an oxide material for use in an oxygen generator. A quantity of dry zirconia particles is blended with Barium Peroxide particles and thereafter heated in a nitrogen atmosphere until the Barium Peroxide melts and coats the zirconia particles. The Barium Peroxide coating is subsequently decomposed to Barium Oxide. The Barium Oxide coated zirconia particles are allowed to cool and then passed through a grinder to produce a uniform particle size for oxide material.
Claims10
A process of manufacturing an oxide material for use in an oxygen extractor, comprising the steps of:
- mixing a quantity of dry zirconia particles with a quantity of barium peroxide particles to create a blended mixture;
- heating said blended mixture in an oven to a temperature of between 500.degree. to 600.degree. C until said barium peroxide particles melt and coat the zirconia particles:
- uniformly increasing the temperature in the oven up to 850.degree. C causing said peroxide coating to decompose to a barium oxide coating;
- cooling the barium oxide coated zirconia particles to room temperature;
- and
- passing the cooled barium oxide coated zirconia particles through a grinder to produce a desired particle size for said oxide material.
In an oxygen generator having an optimum operating range of between 750.degree.-850.degree. C, an oxide composition for reacting with pressurized air to form a higher oxide, said higher oxide reverting to oxide through the release of oxygen in the absence of pressurized air, said composition comprising:
- a zirconia particle;
- and
- a barium oxide coating surrounding said zirconia particle, said zirconia particle absorbing heat generated by the reaction of the oxide composition with air to stabilize the reaction temperature within the operating range of the oxygen generator.
A process for manufacturing an oxide material for use in an oxygen extractor, comprising the steps of:
- treating a quantity of zirconia particles in an oven to a temperature of between 800.degree. to 900.degree. C to remove any water contained therein;
- maintaining the temperature of the zirconia particles at 800.degree. to 900.degree. C for about 1 hour;
- cooling the dry zirconia particles to between 100.degree. to 150.degree. C;
- mixing the dry zirconia particles with a quantity of barium peroxide to create a blended mixture;
- heating said blended mixture in an oven to a temperature of between 500.degree. to 600.degree. C to melt said barium peroxide particles and cost the zirconia particles;
- uniformly increasing the temperature of the peroxide coated zirconia particles causing the barium peroxide coating to decompose to a barium oxide coating;
- cooling the barium oxide coated zirconia particle to about 40.degree. C;
- and
- passing the cooled barium oxide coated zirconia particle through a grinder to produce a desired particle size for said oxide material.
Dependencies are inferred from the claim text.