Process for obtaining seed hull commodities including cellulosic fibers and xylitol

A process for removing cellulosic fibers from uncut and once cut cottonseed hulls having thereon a substantial amount of linters of from about 6 to about 10 millimeters in length and embedded hull fibers of from about 2 to about 4 millimeters in length, which process comprises the sequential steps of:

• (a) in the absence of mechanical action sufficient to cause degradation of fiber properties, pretreating at least one member selected from the group consisting of uncut and once cut cottonseed hulls which member comprises both cellulosic fibers and non-fibrous hull components by agitating them in the presence of steam with from about 2% to about 6% by weight base in alkaline solution based upon the oven-dry weight of the seed hulls at a temperature of from about 80.degree. to about 100.degree. C for a period of from about 50 to about 70 minutes to remove polyphenolic materials from the cottonseed hulls and to soften the cottonseed hulls, (b) separating the softened cottonseed hulls from the alkaline solution, (c) in the absence of mechanical action sufficient to cause degradation of fiber properties, contacting the softened cottonseed hulls in the presence of steam at a temperature of from about 110.degree. to about 130.degree. C, and for a period of from about 45 to about 75 minutes, with an oxygen gas-saturated alkaline solution, the alkaline solution consisting essentially of water and from about 12 to about 18% by weight base selected from the group consisting of sodium hydroxide and sodium carbonate and based upon the oven-dry weight of the cottonseed hulls, with about 120 psi to 150 psi oxygen gas pressure being maintained during said contacting, (d) recovering softened cottonseed hulls and linters from the alkaline solution, (e) washing the softened cottonseed hulls and linters, and (f) fractionating the washed softened cottonseed hulls and linters so as to produce essentially clean cellulosic fibers having substantially unimpaired mechanical properties, said cellulosic fibers comprising (i) linters of from about 6 to about 10 millimeters and (ii) hull fibers of from about 2 to about 4 millimeters in length.

A process for obtaining xylose and readily usable cellulosic fibers from uncut and once cut cottonseed hulls having thereon linter fibers of from about 5 to 15 millimeters in length and embedded hull fibers of from about 1.5 to about 5 millimeters in length, which process comprises:

• (a) in the absence of mechanical action sufficient to cause degredation of fiber properties, pretreating at least one member selected from the group consisting of uncut and once cut cottonseed hulls which member comprises both cellulosic fibers and non-fibrous hull components with alkaline solution at a concentration and temperature and for a time sufficient to remove polyphenolic materials and coloring substances but not appreciable xylan from the seed hulls and to soften the seed hulls;
• (b) separating the softened cottonseed hulls from the alkaline solution;
• (c) in the absence of mechanical action sufficient to cause degredation of fiber properties, contacting the softened cottonseed hulls with an oxygen gas-saturated alkaline solution at a concentration and temperature and for a time sufficient to soften further the seed hulls and render fibers readily separable from the cottonseed hulls and insufficient to remove appreciable xylan from the hulls;
• (d) separating said softened cottonseed hulls and fibers so as to produce (1) essentially clean cellulosic fibers and (2) hull residue comprising xylan, the hull residue being essentially free of polyphenolic materials and coloring substances and essentially free of hull fibers;
• and (e) hydrolyzing the xylan-containing hull residue to convert substantially all of the xylan to xylose and produce a xylose hydrolyzate solution.

A process for obtaining xylose and readily usable cellulosic fibers having substantially unimpaired mechanical properties from ginned, decorticated, uncut and once cut cottonseed hulls having thereon a substantial amount of linters from about 6 to about 10 millimeters in length and embedded hull fibers of from about 2 to about 4 millimeters in length, which process comprises the sequential steps of:

• (a) in the absence of mechanical action sufficient to cause degredation of fiber properties, pretreating at least one member selected from the group consisting of uncut and once cut cottonseed hulls which member comprises both cellulosic fibers and non-fibrous hull components with from about 0.5% to about 10% by weight base in alkali solution based upon the oven-dry weight of the seed hulls at a temperature of from about 80.degree. to about 100.degree. C to remove polyphenolic materials and coloring substances from the cottonseed hulls and to soften the cottonseed hulls;
• (b) separating the softened cottonseed hulls from the alkaline solution;
• (c) in the absence of mechanical action sufficient to cause degredation of fiber properties, contacting the softened cottonseed hulls at a temperature of from about 110.degree. to about 130.degree. C, with an oxygen gas-saturated alkaline solution, the alkaline solution consisting esentially of water and from about 12% to about 18% by weight base selected from the group consisting of sodium hydroxide and sodium carbonate and based upon the oven-dry weight of the cottonseed hulls, to soften further the cottenseed hulls and render the linters readily separable from the hulls;
• (d) recovering the softened cottonseed hulls and linters from the alkaline solution of (c);
• (e) washing the softened cottonseed hulls and linters;
• (f) fractionating said softened cottonseed hulls and linters so as to separate and produce (1) essentially clean cellulosic fibers having substantially unimpaired mechanical properties, said cellulosic fibers comprising (i) linters of from about 6 to about 10 millimeters in length and (ii) hull fibers of from about 2 to about 4 millimeters in length, and (2) hull residue comprising xylan, the hull residue being essentially free of polyphenolic materials and coloring substances and essentially free of the linters and the hull fibers;
• (g) contacting the the xylan-containing hull residue with sulfuric acid at a temperature and concentration and for a time sufficient to convert substantially all of the xylan to xylose and produce a xylose hydrolyzate solution;
• (h) separating the xylose hydrolyzate solution from remaining hull residue;
• and (i) neutralizing the xylose hydrolyzate solution.

A process for obtaining multiple cottonseed hull commodities including xylitol and readily usable cellulosic fibers having substantially unimpaired mechanical properties from ginned, decorticated, uncut and once cut cottonseed hulls having thereon a substantial amount of linters from about 6 to about 10 millimeters in length and embedded hull fibers of from about 2 to about 4 millimeters in length, which process consists essentially of the sequential steps of:

• (a) in the absence of mechanical action sufficient to cause degradation of fiber properties, pretreating at least one member selected from the group consisting of uncut and once cut cottonseed hulls which member comprises both cellulosic fibers and non-fibrous hull components by agitating them in the presence of steam with from about 2% to about 6% by weight of alkali in alkaline solution based upon the oven-dry weight of the seed hulls at a temperature of from about 80.degree. to about 100.degree. C for a period of from about 50 to about 70 minutes to remove polyphenolic materials and coloring substances from the cottonseed hulls and to soften the cottonseed hulls;
• (b) separating the softened cottonseed hulls from the alkaline solution;
• (c) in the absence of mechanical action sufficient to cause degradation of fiber properties, contacting the softened cottonseed hulls in the presence of steam at a temperature of from about 110.degree. to about 130.degree. C, and for a period of from about 45 to 75 minutes, with an oxygen gas-saturated alkaline solution, the alkaline solution consisting essentially of water and from about 12% to 18% by weight base selected from the group consisting of sodium hydroxide and sodium carbonate and based upon the oven-dry weight of the cottonseed hulls, with about 120 psi to 150 psi oxygen gas pressure being maintained during said contacting, to soften further the cottonseed hulls and render the linters readily separable from the hulls;
• (d) recovering the softened cottonseed hulls and linters from the alkaline portion of (c);
• (e) washing the softened cottonseed hulls and linters;
• (f) fractionating said softened cottonseed hulls and linters so as to separate and produce (1) essentially clean cellulosic fibers having substantially unimpaired mechanical properties, said cellulosic fibers comprising (i) linters of from about 6 to about 10 millimeters in length and (ii) hull fibers of from about 2 to about 4 millimeters in length, and (2) hull residue comprising xylan, the hull residue being essentially free of polyphenolic materials and coloring substances and essentially free of the linters and the hull fibers;
• (g) contacting the xylan-containing hull residue with sulfuric acid at a temperature and concentration and for a time sufficient to convert substantially all of the xylan to xylose and produce a xylose hydrolyzate solution;
• (h) separating the xylose hydrolyzate solution from remaining hull residue;
• (i) neutralizing the xylose hydrolyzate solution;
• (j) catalytically hydrogenating the xylose hydrolyzate solution to convert xylose to xylitol;
• and (k) crystallizing xylitol crystals directly from the hydrogenated hydrolyzate solution.