Paper-like thermoplastic film
AssigneeDu Pont Canada Inc.
InventorVaclav George Zboril
Life of this patent
Estimating the term…
Abstract
A paper-like thermoplastic film and a process for making it are disclosed. The process involves extruding a mixture of (a) 70-98% by weight of a polyethylene having a maximum melt flow index of 5 decigrams per minute and (b) 2-30% by weight of inorganic lamellar filler particles, e.g., mica, the largest dimension of said particles being less than 150 microns, through a circular die, in the form of seamless tubing, continuously withdrawing the tubing from the point of extrusion, and expanding and simultaneously cooling the tubing while in the plastic formative state at a temperature above the melting temperature to a blow up ratio in the range of from 1.2:1 to 10:1.
Claims18
A paper-like, voidless, thermoplastic film having a thickness of from 0.3 mil to 10 mil, said film having been made by a process consisting essentially of the steps of extruding a mixture of
- a. 70-98% by weight of a polyethylene having a maximum melt flow index of 5 decigrams per minute, and a density in the range of 0.945 to 0.970 grams per cubic centimeter, and
- b. 2-30% by weight of inorganic lamellar filler particles, the largest dimension of said particles being less than 150 microns and said particles having a minimum particle diameter to particle thickness ratio of about 5:1,
- through a circular die, in the form of a seamless tubing, continuously withdrawing the tubing from the point of extrusion, expanding and simultaneously cooling the tubing while in the plastic formative state to a blow up ratio in the range of from 1.2:1 to 10.1.
A process for producing a paper-like thermoplastic film having a thickness of from 0.3 mil to 10 mil, consisting essentially of the steps of extruding a mixture of
- a. 70-98% by weight of a polyethylene having a maximum melt flow index of 5 decigrams per minute, and a density in the range of 0.945 to 0.970 grams per cubic centimeter, and
- b. 2-30% by weight of inorganic lamellar filler particles, the largest dimension of said particles being less than 150 microns and said particles having a minimum particle diameter to particle thickness of about 5:1,
- through a circular die, in the form of a seamless tubing, continuously withdrawing the tubing from the point of extrusion, expanding and simultaneously cooling the tubing while in the plastic molten state at a temperature above the solidification temperature to a blow up ratio in the range of from 1.2:1 to 10:1.
Dependencies are inferred from the claim text.