Lustrous, antisoiling flame retardant acrylic fibers and process therefor
AssigneeAmerican Cyanamid Company
InventorArutun Maranci
Life of this patent
Estimating the term…
Abstract
Acrylic fibers of a fiber-forming first acrylonitrile polymer containing at least 50% acrylonitrile, a flame retardant amount of a halogen-containing vinyl monomer, and any balance of a halogen-free vinyl monomer having heterogeneously dispersed therein a small amount of an incompatible, halogen-free, second acrylonitrile polymer containing at least 70% acrylonitrile and one or more halogen-free vinyl monomers. The fibers are prepared by wet-spinning an intimate mixture of the polymers separately dissolved in aqueous inorganic solutions of the same salt following conventional procedures but including a hot-wet relaxation of the stretched wet-gel filaments prior to drying.
Claims10
A flame retardant acrylic fiber having a luster value of at least about 17.5% and a light transmission of less than about 25% which comprises a first fiber-forming acrylonitrile polymer containing at least 50 weight percent acrylonitrile, an amount of a halogen-containing vinyl monomer sufficient to impart flame retardancy to said fiber, and any balance of a halogen-free vinyl monomer, and heterogeneously dispersed within said first polymer, a second acrylonitrile polymer free from any halogen content and containing at least 70 weight percent acrylonitrile and any balance of one or more halogen-free vinyl monomers, said second polymer being incompatible with said first polymer and being present in an amount of about 2 to 15 weight percent based on the total weight of said first and second polymers.
A process for preparing a flame retardant acrylic fiber having a luster value of at least about 17.5% and a light transmission of less than about 25% which comprises the steps of:
- (a) preparing a first solution in an aqueous inorganic salt solvent of a fiber-forming first acrylonitrile polymer containing at least 50 weight percent acrylonitrile, a flame retardant, halogen-containing vinyl monomer in an amount sufficient to impart flame retardancy to said fiber and any balance of a halogen-free vinyl monomer;
- (b) preparing a second solution in an aqueous solvent of the same inorganic salt used in step (a) of a second acrylonitrile polymer free from any halogen content and incompatible with said first polymer, said second polymer containing at least 70 weight acrylonitrile and any balance of one or more halogen-free vinyl monomers;
- (c) intimately mixing said second solution in said first solution so as to form a spinning composition in which the polymer content is 98 to 85 weight percent of said first polymer and, correspondingly 2 to 15 weight percent of said second polymer, said percentages totaling 100;
- (d) extruding said spinning composition into an aqueous coagulant to form wet-gel filaments;
- (e) washing the wet-gel filaments free of solvent;
- (f) stretching the washed wet-gel filaments to provide suitable orientation;
- (g) relaxing the stretched wet-gel filaments under hot-wet conditions;
- and thereafter drying the relaxed filaments.