Production of ferrochrome alloy
AssigneeOntario Research Foundation
InventorsAllan M. Smellie, Hans G. Brandstatter
Life of this patent
Estimating the term…
Abstract
Chromium or other metal carbides are recovered from chromates or equivalent soluble metal salts in substantially pure form by solid state carburization. The chromates may be derived from low grade ore to provide an overall non-smelting procedure which is non-polluting. The carbide may be formed into sponge metal.
Claims6
A process for the production of a ferrochrome alloy, which comprises forming an intimate admixture of finely-divided carbon, sodium chromate or sodium dichromate and an iron oxide, and reducing said sodium chromate or sodium dichromate and said iron oxide by an in situ solid state reaction in a reaction zone to form a ferrochrome alloy, said intimate admixture containing sufficient proportions of the components thereof to provide a ferrochrome alloy from said reducing step containing 55 to 66% Cr, 7 to 8% C and the balance Fe, said solid state reaction being carried out at a temperature of about 1025.degree. C to about 1425.degree. C while carbon monoxide formed in said solid state reaction is removed from said reaction zone.
A process for the production of a ferrochrome alloy from a low grade chromite ore, which comprises:
- roasting a low grade chromite ore containing chromium, iron, aluminum and silicon values or a concentrate thereof with sodium carbonate in the presence of oxygen to solubilize substantially all the chromium and at least part of the aluminum and silicon values of said ore while leaving said iron values substantially unaffected;
- leaching said roasted ore to separate soluble compounds from gangue constituents including said iron values and the remainder of said aluminum and silicon values;
- acidifying the leach solution to cause deposition of said soluble aluminum and silicon values;
- separating the deposited materials from the acidified solution to provide an aqueous solution of sodium chromate or sodium dichromate and a sodium carbonate;
- slurrying iron values in said separated gangue constituents and finely-divided carbon in said aqueous solution;
- evaporating the resulting slurry to dryness to form an intimate admixture of carbon, sodium chromate or sodium dichromate, sodium carbonate and iron oxide;
- reducing said sodium chromate or sodium dichromate and said iron oxide with said carbon by an in situ solid state reaction in a reaction zone to form a ferrochrome alloy;
- controlling the relative proportions of the components of said intimate admixture to provide said ferrochrome alloy which contains 55 to 60% Cr, 7 to 8% C and the balance Fe;
- effecting said solid state reaction at a temperature of about 1025.degree. C to about 1425.degree. C while carbon monoxide formed in said solid state reaction is removed from said reaction zone;
- leaching the solid resulting from said reducing step to form an aqueous solution of sodium carbonate and leave said ferrochrome alloy in the solid phase;
- separating said ferrochrome alloy from said sodium carbonate solution;
- recovering said sodium carbonate from said sodium carbonate solution thereof;
- and
- recycling said recovered sodium carbonate to said roasting step as at least part of the sodium carbonate utilized therein.