Silicon nitride NGV's and turbine blades
AssigneeThe Secretary of Defence, in Her Brittanic Majesty's Government of the United Kingdom of Great Britain and Northern Ireland
InventorJack Raymond Bird
Life of this patent
Estimating the term…
Abstract
The invention concerns a method of making an article from silicon nitride powder and a fluxing agent. The method comprises hot pressing a first section of the silicon nitride article, transferring the pressed section to a further mould large enough to accomodate sufficient silicon nitride powder and fluxing agent to produce the other section of the article, and subsequently hot pressing the contents of the mould to solidify the silicon nitride powder and fluxing agent into the second section of the article which becomes bonded to the first section.
Claims7
A method of manufacturing a unitary article from hot pressed silicon nitride having at least two portions, each portion thereof being formed in a separate hot pressing operation, the formed article having at least two sections of differing wall thickness, the method including the steps of
- a. hot pressing a first mixture of silicon nitride powder and a fluxing agent for said silicon nitride in a first mold to form a first one of the said sections,
- b. placing said first section in a second mould which is adapted to accommodate both of the said sections,
- c. filling the mould with a sufficient quantity of silicon nitride powder and a fluxing agent for said silicon nitride to form the second one of the said sections by not pressing the said second mixture, and
- d. hot pressing said second mixture, the resultant to densify the added silicon nitride powder and fluxing agent together to form a second section, while at the same time bonding said second section to the said first section, the entire article completely densified throughout.