Process for preparing anhydrous aluminum fluoride
AssigneeCentral Glass Company, Limited
InventorsTetsuhiro Ono, Minoru Aramaki, Etuo Ushirogouthi
Life of this patent
Estimating the term…
Abstract
Ammonium tetrafluoroaluminate particles having an average particle size above 50.mu. are reacted with an aluminum compound such as aluminum hydroxide or oxide first at a temperature of 250.degree. C to 300.degree. C and then at a temperature of 350.degree. to 500.degree. C to form crystalline particles of anhydrous aluminum fluoride (II) with an average particle size almost corresponding to the starting ammonium tetrafluoroaluminate. The heating of the crystalline particles to a temperature above 550.degree. C results in formation of aluminum fluoride (I) with a large average particle size.
Claims5
A process for preparing crystalline particles of anhydrous aluminum fluoride having a relatively large particle size and excellent flowability, said process comprising the steps of interacting ammonium hexafluoroaluminate, an inorganic acid selected from the group consisting of sulfuric acid and hydrochloric acid and an aluminum compound selected from the group consisting of aluminum hydroxide and aluminum oxide at a temperature of below 100.degree. C to obtain ammonium tetrafluoroaluminate particles having an average size of above 50 microns;
- interacting said ammonium tetrafluoroaluminate particles having an average size above said 50 microns and an aluminum compound selected from the group consisting of aluminum compound selected from the group consisting of aluminum hydroxide and aluminum oxide first, at a temperature of from between about 250.degree. to 300.degree. C to decompose the ammonium tetrafluoroaluminate into .gamma.-aluminum fluoride, NH.sub.4 HF.sub.2 and NH.sub.3 and then at a temperature of between about 350.degree. to 500.degree. C to react said NH.sub.4 HF.sub.2 with said aluminum compound to thereby obtain crystalline particles of .gamma.-anhydrous aluminum fluoride having an average particle size corresponding essentially to that of the starting ammonium tetrafluoroaluminate.
A process for preparing crystalline particles of anhydrous aluminum fluoride having a relatively large particle size and excellent flowability, said process comprising the steps of interacting ammonium tetrafluoroaluminate particles having an average size above 50 microns and an aluminum compound selected from the group consisting of aluminum hydroxide and aluminum oxide first at a temperature of from between 250.degree. to 300.degree. C to decompose the ammonium tetrafluoroaluminate into .gamma.-aluminum fluoride, NH.sub.4 HF.sub.2 and NH.sub.3 and then at a temperature of between about 350.degree. to 500.degree. C to react said NH.sub.4 HF.sub.2 with said aluminum compound to thereby obtain crystalline particles of .gamma.-anhydrous aluminum fluoride having an average particle size corresponding essentially to that of the starting ammonium tetrafluoroaluminate, said process further comprising heating said crystalline particles of said .gamma.-anhydrous aluminum fluoride to a temperature above 550.degree. C under agitation conditions of a peripheral speed of above 10 m/min. to thereby produce crystals of .alpha.-anhydrous aluminum fluoride.
Dependencies are inferred from the claim text.