Acrylic modified foamed nylon product and process
AssigneeRohm and Haas Company
InventorMarshall T. Purvis
Life of this patent
Estimating the term…
Abstract
A method of making nylon (polycarbonamide) foam involving the use of a multi-phase carboxylic acid-containing polymer which reacts with the amine groups of the nylon to produce water which blows the foam during the process.
Claims8
A method of making polycarbonamide foam comprising extruding a blend of polycarbonamide, characterized as possessing amine end groups with recurring amide linkages, and a multiphase carboxylic acid-containing polymer, which has a first elastomeric phase formed by polymerization of a monomer charge of 50 to 99.9 parts by weight alkyl acrylate, wherein the alkyl group contains 1 to 15 carbon atoms, butadiene or substituted butadiene;
- 0 to 40 parts by weight of other ethylenically unsaturated monomers;
- 0 to 5 parts by weight of a graft-linking monomer;
- and a final phase polymerized in the presence of said first phase from a monomer charge comprising 0.1 to 50 parts by weight of a copolymerizable carboxylic acid;
- 50 to 99.9 parts by weight of a member selected from the group consisting of alkyl methacrylate, styrenes, acrylonitrile, methacrylonitrile, and olefins that, when homopolymerized, form polymers having a heat distortion temperature greater than about 20.degree. C, in a non-vented extruder under conditions such that the carboxylic acid groups of said multiphase carboxylic acid-containing polymers react with the amine groups of acid polycarbonamide, said multiphase polymer having a final polymeric phase polymerized in the presence of a first polymeric phase, wherein the polycarbonamide foam has a density less than 1 without the use of added blowing agents.
The method of claim 5 wherein said alkyl acrylate comprises butyl acrylate.
A method of making polycarbonamide foam comprising introducing a blend of polycarbonamide, characterized as possessing amine end groups with recurring amide linkages, and a multiphase carboxylic acid-containing polymer, which has a first elastomeric phase formed by polymerization of a monomer charge of 50 to 99.9 parts by weight alkyl acrylate, wherein the alkyl group contains 1 to 15 carbon atoms, butadiene or substituted butadiene;
- 0 to 40 parts by weight of other ethylenically unsaturated monomers;
- 0 to 5 parts by weight of a graft-linking monomer;
- and a final phase polymerized in the presence of said first phase from a monomer charge comprising 0.1 to 50 parts by weight of a copolymerizable carboxylic acid;
- 50 to 99.9 parts by weight of a member selected from the group consisting of alkyl methacrylate, styrenes, acrylonitrile, methacrylonitrile, and olefins that, when homopolymerized, form polymers having a heat distortion temperature greater than about 20.degree. C, in a compression mold, molding at a first pressure under heat so as to cause reaction between the amine groups of the polycarbonamide and the acid groups of the multiphase polymer, then reducing the pressure so as to cause the melted blend to foam due to steam being formed in situ, wherein the polycarbonamide foam has a density less than 1 without the use of added blowing agents.
Dependencies are inferred from the claim text.