Dual cure cathodic electrocoating compositions
AssigneeSCM Corporation
InventorVincent Daniel McGinniss
Life of this patent
Estimating the term…
Abstract
An electrocoating composition containing a polymer having pendant tertiary amine groups, a polymer containing pendant mercaptan groups, an apha-, beta-ethylenically unsaturated carbonyl cross-linking agent, and a photosensitizer can be electrodeposited onto a cathode substrate disposed within an aqueous electrocoating bath. Full cure of the electrodeposited coating on the cathode substrate is obtained by the combination of heat curing and ultraviolet radiation curing. In a specific embodiment of the present invention, a single polymer contains both the pendant tertiary amine groups and pendant mercaptan groups.
Claims10
A cathodic electrocoating composition dispersed in an aqueous electrocoating bath for electrodeposition onto a cathode substrate disposed within said bath for forming a curable electrodeposited coating on said cathode substrate, comprising:
- a. a water-dispersed electrocoating polymer having at least about 1% by weight pendant mercaptan groups;
- b. a water-dispersed electrocoating polymer having at least about 1% by weight pendant tertiary amine groups, each said amine group being attached to an alpha carbon of said polymer;
- c. at least about 5% by weight of said polymers of an alpha-, beta- ethylenically unsaturated carbonyl cross-linking agent having at least two alpha-, beta-ethylenically unsaturated carbonyl groups;
- and
- d. at least about 0.5% ultraviolet photosensitizer by weight of said polymers;
- said pendant amine groups and said pendant mercaptan groups together comprising at least about 5% by weight of said polymers, said electrodeposited coating of said electrocoating composition adapted to cure by heating said electrodeposited coating on said cathode substrate to cross-link said mercaptan groups with said cross-linking agent to partially cure said coating followed by irradiating with ultraviolet radiation said partially cured coating to cross-link said alpha carbon of said polymer having said pendant amine groups with said cross-linking agent to fully cure said coating on said cathode substrate.
A cathodic electrocoating composition dispersed in an aqueous electrocoating bath for electrodeposition onto a cathode substrate disposed within said bath for forming a curable electrodeposited coating on said cathode substrate, comprising:
- a. a water-dispersed electrocoating polymer having at least about 1% by weight pendant mercaptan groups and said polymer having at least about 1% by weight pendant tertiary amine groups, each said amine group being attached to an alpha carbon of said polymer, the total proportion of both said amine groups and said mercaptan groups being at least about 5% by weight of said polymer;
- b. at least about 5% by weight of said polymers of an alpha-, beta-ethylenically unsaturated carbonyl cross-linking agent having at least two alpha-, beta-ethylenically unsaturated carbonyl groups;
- and
- c. at least 0.5% ultraviolet photosensitizer by weight of said polymer said electrodeposited coating on said cathode substrate adapted to cure by heating said electrodeposited coating to cross-link said pendant mercaptan groups which said cross-linking agent to partially cure said coating, followed by irradiating with ultraviolet radiation said partially cured coating to croslink said alpha carbon with said cross-linking agent to fully cure said coating on said cathode substrate.
Dependencies are inferred from the claim text.