Process for the passivation of sponge iron utilizing reducing gases containing free oxygen
AssigneeUnited States Steel Corporation
InventorStephen Waslo
Life of this patent
Estimating the term…
Abstract
Passivation of sponge iron by a mild reoxidation thereof is effected by contact, at a temperature of 200.degree. to 600.degree. F, with a gaseous atmosphere consisting essentially of 25 to 80% H.sub.2, 15 to 70% CO and 0.5% to 4.0% O.sub.2 for a time in excess of about 1 hour. The passivation atmosphere may be produced by dilution of a free-oxygen-containing gas with conventional reducing gases. Therefore, the process is particularly amenable to the in-line passivation of hot reduced pellets i.e. wherein passivation may be effected directly within the lower portion of a shaft furnace.
Claims10
A process for the passivation of sponge iron which comprises, contacting the sponge iron at a temperature within the range of 200.degree. to 600.degree. F with a passivation atmosphere consisting essentially of 25 to 80% H.sub.2, 15 to 70% CO and 0.5 to 4% O.sub.2, for a time of about 1 to 3 hours, and wherein the time employed is greater than about 1.5 hours when said O.sub.2 concentration is below about 0.8%.
In the direct reduction of iron ore pellets in a shaft furnace wherein said pellets are permitted to substantially continuously descend in said shaft furnace, and are contacted in a first zone with a reducing gas which is substantially composed of the effluent resulting from the reforming of natural gas or carbonaceous fuels, said reducing gas containing (i) H.sub.2 and CO.sub.2 in the sum of 85 to 95% and (ii) residual constituents comprising CO.sub.2, CH.sub.4, N.sub.2 and H.sub.2 O, said contact being effected at a temperature 1400.degree. to 1750.degree. F for a time sufficient to produce a sponge iron product,
- the improvement for passivating said sponge iron in an in-line process which comprises, in a second zone, at a temperature of 200.degree. - 600.degree. F, contacting said sponge iron with a passivation atmosphere consisting essentially of 25 to 80% H.sub.2, 15 to 70% CO and 0.5 to 4% O.sub.2, said contact being for a period of about 1 hour to 3 hours and wherein the time employed is greater than about 1.5 hours when said O.sub.2 concentration is below about 0.8%.