Heat-activatable polyurethane powder coatings
AssigneeE. I. Du Pont de Nemours and Company
InventorGuenther Kurt Hoeschele
Life of this patent
Estimating the term…
Abstract
A heat-activatable polyurethane powder composition is prepared which contains both epoxy and amino end groups, the distribution of which is determined by the order in which the reactants are brought together. When the powder is deposited on a substrate and heated above its melting point, the epoxy groups react with the active hydrogens available from the amino groups, resulting in the formation of a high molecular weight polyurethane film.
Claims25
In a process for forming a heat-activatable polyurethane powder characterized by low-melt viscosity upon initial melting, and in which powder the particles are generally bead-like in form, the improvement consisting essentially of (1) reacting
- a. one mole of polymeric glycol having a number average molecular weight of about 400-4,000,
- b. X moles of a diol having a molecular weight less than about 250 wherein X = 0-20,
- c. Y moles of an organic diisocyanate wherein Y = 1.03 (1 + X) to 1.60 (1 + X), d. Z moles of a monohydroxy-epoxide wherein Z = 0.0286 (1 + X) to 1.000 (1 + X),
- e. 0.7 (2Y-2-X-Z-2) to 1.0 (2Y-2X-Z-2) moles of a short chain diamine, and (2) selecting the amounts of reactants (d) and (e) so that the polyurethane powder formed will contain 0.2 to 1.1 amino groups per epoxy group, and wherein (3) the size and shape of bead particles is achieved by initially emulsifying reactants (a) and (b) in an inert organic solvent with the aid of a surfactant, followed by converting said emulsion to a dispersion of finely-divided polyurethane beads and recovering the latter.
A process for forming a heat-activatable polyurethane powder which comprises the steps of (1) emulsifying with the aid of a surfactant one mole of a polymeric glycol or a mixture thereof with X moles of a low molecular weight diol wherein X = 0 - 20 in an inert organic liquid, (2) contacting the resulting emulsion with 1.03 (1 + X) to 1.60 (1 + X) moles of an organic diisocyanate, (3) allowing the diisocyanate to react with the polymeric glycol or mixture thereof with a low molecular weight diol in the emulsion to form an --NCO-terminated polyurethane dispersed in said inert liquid, (4) contacting the resulting dispersion with a hydroxy-epoxide, (5) permitting the aforesaid epoxide to react with about 48 to 83% of the free --NCO groups of the dispersed polyurethane to form a polyurethane partially terminated with epoxy groups, (6) contacting the resulting dispersion with 0.7 to 1.0 moles of a diamine per equivalent of --NCO groups remaining after step (5) and then reacting the diamine with --NCO groups of said polyurethane to provide the polyurethane with free amino groups, and (7) separating the dispersed polyurethane as a finely-divided powder, the particles of said powder providing epoxide-terminated urethane groups and terminal amino groups in such amounts that when the powder is heated the epoxy groups will react with said amino groups to substantially increase the molecular weight of said polyurethane.
A process for forming a heatactivatable polyurethane powder comprising the steps of (1) emulsifying with the aid of a surfactant one mole of a polymeric glycol, or a mixture thereof with X moles of a low molecular weight diol wherein X = 0 - 20, and 0.0286 (1 + X) to 1.00 (1 + X) moles of a hydroxy-epoxide in an inert organic liquid, (2) contacting the resulting emulsion with 1.03 (1 + X) to 1.60 (1 + X) moles of an organic diisocyanate, (3) allowing the diisocyanate to react with said polymeric glycol or mixture thereof with said diol with said epoxide to form a dispersion of polyurethane in which some of the --NCO groups are still present, (4) contacting the resulting dispersion with 0.7 to 1.0 moles of a diamine per equivalent of -NCO groups remaining after step (3) and then reacting the latter with the residual --NCO groups of said polyurethane to provide the polyurethane with free amino groups, and (5) separating the dispersed polyurethane as a finely-divided powder, the particles of said powder providing epoxy-terminated urethane groups and amino groups in such amounts that when the powder is heated the epoxy groups will react with said free amino groups to substantially increase the molecular weight of said polyurethane.
A process for making particles of a polyurethane powder having epoxy-terminated urethane groups, which can serve as one component of a heat-activatable polyurethane powder composed of a mixture of two separate types of particles, one type having epoxy-terminated urethane groups, and the second having terminal amino groups, so that said mixture provides suitable amounts of each type, said process comprising forming the first type of particles by the steps of (1) mixing a polymeric polyol, or a mixture thereof with a low molecular weight diol, and a hydroxy-epoxide in an inert organic liquid in which said polymeric glycol or mixture thereof with a low molecular weight diol is insoluble and forming an emulsion thereof with the aid of a surfactant, (2) contacting the resulting emulsion with an organic diisocyanate, (3) allowing the diisocyanate to react with said polyol or a mixture thereof with a low molecular weight diol, and with said epoxide to form a dispersion of polyurethane containing epoxy-terminated urethane groups, and (4) separating the resulting product as a finely-divided powder.
A process for forming a heat-activatable polyurethane powder composed of a mixture of two separate types of particles, one type having epoxy-terminated urethane groups and the other type having terminal amino groups, comprising
- A. forming the first type of particles by the steps of (1) emulsifying with the aid of a surfactant one mole of a polymeric glycol or a mixture thereof with X moles of a low molecular weight diol wherein X = 0 - 20 in an inert organic liquid, (2) contacting the emulsion with 1.03 (1 + X) to 1.60 (1 + X) moles of an organic diisocyanate, (3) allowing the diisocyanate to react with said polymeric glycol or mixture thereof with low molecular weight diol in the emulsion to form an -NCO-terminated polyurethane dispersed in said inert organic liquid, (4) contacting the resulting dispersion with 0.06 (1 + X) to 1.20 (1 + X) moles of a hydroxy-epoxide, (5) permitting the latter to react with essentially all of the free -NCO groups of the dispersed polyurethane to form an epoxy-terminated polyurethane, and (6) separating the dispersed polyurethane as a finely-divided powder,
- B. forming the second type of particles by the steps of (1) emulsifying with the aid of a surfactant one mole of a polymeric glycol or a mixture thereof with X moles of a low molecular weight diol wherein X = 0 - 20 in an inert organic liquid, (2) contacting the emulsion with 1.03 (1 + X) to 1.60 (1 + X) moles of an organic diisocyanate, (3) allowing the diisocyanate to react with said polymeric glycol or mixture thereof with low molecular weight diol in the emulsion to form an --NCO-terminated polyurethane dispersed in said organic liquid, (4) contacting the resulting dispersion with 0.7 to 1.0 moles of a diamine per equivalent of --NCO groups remaining after step (3) to react the latter with the available --NCO groups of the dispersed polyurethane to provide terminal groups, and (5) separating the resulting product as a finely-divided powder;
- and mixing the two types of particles in such proportions that the ratio of amino groups to epoxy groups is 0.2/1.0 to 1.1/1.0.
Dependencies are inferred from the claim text.