Loading patent…
AssigneeFMC Corporation
InventorsCharles F. Ferraro, Richard A. Javick, James A. Robertson
Estimating the term…
Finely-divided, water dispersible, low molecular weight, linear polyamide resin particles having a unique morphology and of uniform particle sizes are formed by preparing a linear polyamide of a predetermined low molecular weight in the presence of water followed by rapidly quenching the reaction mass with an aqueous medium below the freezing point of the polyamide and continuing the cooling of the mass to a temperature sufficiently low so as to prevent particle growth and structural alteration while regulating the pH of the quenched mass to provide particles of predetermined, uniform size dispersed in the aqueous medium. The particles vary from ultimate flaky sheets or lamellae to loosely packed, randomly oriented, clusters of flaky sheets. Spray dried products may be agglomerates which disintegrate readily in water to the original particles or aggregates depending upon intended uses. The dispersions and dried products are useful in the coating art and the polyamide may be polymerized to high molecular weights after application to a substrate.
As an article of manufacture, free flowing, spray dried low molecular weight, linear polyamide resin powder having a reduced viscosity of between about 0.1 and about 0.4, consisting essentially of loosely bound agglomerates of loosely packed, randomly oriented, clusters of flaky sheets, the flaky sheets having a mean particle size between 0.03 micron and about 6 microns and the particle size distribution is about d.+-.0.8d where d is the means particle size, the agglomerates having a size within a range of between about 3 microns and about 150 microns and being further characterized in that when dispersed in water the agglomerates disintegrate into loosely packed, randomly oriented, clusters to flaky sheets having particle sizes of approximately the same size and size distribution as the original flaky sheets and form a stable dispersion of flaky sheets.
The method of forming free-flowing, low molecular weight, linear polyamide resin powder which comprises mixing a least one polyamide forming monomer or high molecular weight, linear polyamide and water, heating the mixture under pressure to a temperature sufficiently high and for a period sufficient to form a linear polyamide of a predetermined low molecular weight, the temperature exceeding the melting point of the formed polyamide, thereafter instantaneously quenching the heated mixture in an aqueous quenching medium to instantaneously reduce the temperature of the heated mixture to a temperature below the freezing point of the formed polyamide and to bring the mass to a pH between about pH.sub.3 and pH.sub.9 thereby converting the formed polyamide into finely-divided, water dispersible, low molecular weight, linear polyamide resin particles having particle sizes within a narrow particle size distribution and to instantaneously reduce the temperature of the mass to a temperature where particle growth is prevented and the particle size and structure is retained, recovering a stable aqueous dispersion of the finely-divided, low molecular weight, linear polyamide resin particles in the form of loosely packed, randomly oriented clusters of flaky sheets in the aqueous medium, spray drying the recovered stable aqueous dispersion and recovering a free-flowing, low molecular weight, linear polyamide resin powder consisting essentially of loosely bound agglomerates of loosely packed, randomly oriented, clusters of flaky sheets.
Dependencies are inferred from the claim text.