Process for finishing a nonwoven film-fibril sheet

A process for preparing a bonded nonwoven sheet of polyethylene film-fibrils, said sheet having high delamination strength and uniformity of appearance, said process comprising

• 1. providing a lightly consolidated, non-woven, film-fibril sheet having a basis weight of from about 34-119 g/m.sup.2 (1-3.5 oz/yd.sup.2), a coefficient of variation in basis weight, normalized to a 68 g/m.sup.2 (2 oz/yd.sup.2) basis weight, of from about 8 - 15%, and a density of from about 0.2-0.4 g/cc;
• 2. passing the lightly consolidated sheet through a nip formed between two rolls while applying a nip loading sufficient to provide an average nip pressure of from about 1.7-6.2 MPa (250-900 psi);
• one of said rolls having a multiplicity of bosses over practically its entire surface and extending from the surface of the roll to a height of from about 50-100% of the thickness of the lightly consolidated sheet, said bosses having tips which have at least one dimension being less than 0.64 cm (0.25 in) and the most prominent of which, in aggregate, form an area which is from about 1-50% of the area of the surface of the roll;
• the other roll having a surface with a durometer hardness of from about 55-80 as measured on the Shore D scale;
• 3. passing the resulting sheet, while under restraint, through a heating zone and raising the temperature of one surface of the sheet sufficiently to cause fusion of surface film-fibrils so as to obtain a sheet having an abrasion resistance of at least two cycles and cooling the sheet, while under restraint to a temperature below that at which the sheet distorts or shrinks;
• and
• 4. repeating step (3) with the opposite side of the sheet to obtain a bonded sheet with an opacity of more than about 72% but less than about the value obtained from the equation, % opacity = 92 - 1.9 .sqroot.121 - basis weight, said basis weight being the basis weight of the finished product in g/m.sup.2.