US 4,067,955 AGranted

Method of forming a silicon carbide article

AssigneeFord Motor Company

InventorsJack E. Noakes, Hiroshi Sato, Leslie L. Terner

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method of forming a silicon carbide article is disclosd. Selected weight percentages of silicon carbide particles, graphite particles, if desired, and a thermosetting binder are mixed together and molded into an article by molding techniques which operate on the basis that the thermosetting binder forms a continuous medium about all the particles supported therein. The molded article is heated in the absence of oxygen and the thermosetting binder breaks down to form a low density, vitreous carbon phase. The article is heated in the absence of oxygen to a selected temperature at which the article is maintained for a period of time in a gaseous environment consisting of nitrogen preferably with a small amount of hydrogen therein. The hydrogen-nitrogen treatment is effective to cleanse the article and insure that there is an adequate pore structure through the article for a later siliciding operation to be carried out thereon. The article is silicided at an elevated temperature by penetration of the article through its pore structure with a reactable form of silicon.

Claims4

Dependent claims

In a method of forming a silicon carbide article:

(a) wherein 60-80% by weight of silicon carbide particles having an average particle size in the range from about 40 microns to less than 1 micron are mixed together with 40-20% by weight of a thermosetting binder which produces a flowable liquid phase when melted and which produces carbon upon nonoxidative pyrolysis, said silicon carbide particles also having oxides of silicon present therein as an impurity;
(b) wherein the mixture is heated to a temperature whereat the thermosetting binder is in a liquid phase;
(c) wherein the mixture is injection molded by an injection molding technique to form an article, the injection molding technique operating on the basis that the flowable thermosetting binder forms a continuous phase about the silicon carbide particles supported therein;
(d) wherein the thermosetting binder is stiffened to lend strength to the molded article so that it may be removed from its mold;
(e) wherein the molded article is pyrolized in the absence of oxygen so that the thermosetting binder undergoes a volumetric reduction while breaking down to form a vitreous carbon phase which serves to bond silicon carbide particles together, this action also developing pores throughout the article;
and (f) wherein the article is silicided at an elevated temperature by permitting the penetration of the article through its pores with silicon which reacts with the vitreous carbon to form silicon carbide;
the improvement which comprises by addition of a new step between steps (e) and (f), a step which comprises:
treating the article after it has been pyrolized and prior to the siliciding thereof by maintaining the article once it has been heated to a temperature of at least 2800.degree. F for a period of time in a gaseous environment consisting of a nitrogen-hydrogen atmosphere in a range of from 3% by volume to 7% by volume hydrogen whereby the hydrogen reacts with some of the vitreous carbon phase in the article to remove a portion of the carbon in the article and insure that volume is available in the article to accommodate conversion of the article's remaining carbon to silicon carbide, and whereby the nitrogen reacts with oxides of silicon present in the article to transform the oxides to silicon nitride.

5 more elements

In a method of forming a silicon carbide article:

(a) wherein 60-75% by weight of silicon carbide particles having an average particle size in the range from about 40 microns to less than 1 micron and 0 to 7% by weight of graphite having an average particle size in the range from about 10 to 0.1 microns are mixed together with 40-23% by weight of a thermosetting binder which produces a flowable liquid phase when melted and which produces a carbon upon nonoxidative pyrolysis, said silicon carbide particles also having oxides of silicon present therein as an impurity;
(b) wherein the mixture is heated to a temperature whereat the thermosetting binder is in a liquid phase;
(c) wherein the mixture is injection molded by an injection molding technique to form an article, the injection molding technique operating on the basis that the flowable thermosetting binder forms a continuous phase about the silicon carbide particles supported therein;
(d) wherein the thermosetting binder is stiffened to lend strength to the molded article so that it may be removed from its mold;
(e) wherein the molded article is pyrolized in the absence of oxygen so that the thermosetting binder undergoes a volumetric reduction in breaking down to form a vitreous carbon phase which serves to bond the silicon carbide particles together, this action also developing pores throughout the article;
and (f) wherein the article is silicided at an elevated temperature by permitting the penetration of the article through its pores with silicon which reacts with the vitreous carbon to form silicon carbide;
the improvement which comprises by addition of a new step between steps (e) and (f), a step which comprises:
treating the article after it has been pyrolized and prior to the siliciding thereof by maintaining the article once it has been heated to a temperature of at least 2800.degree. F for a period of time in a gaseous environment consisting of a nitrogen-hydrogen atmosphere in a range of from 3% by volume to 7% by volume hydrogen whereby the hydrogen reacts with some of the vitreous carbon phase in the article to remove a portion of the carbon in the article and insure that volume is available in the article to accommdate conversion of the article's remaining carbon to silicon carbide, and whereby the nitrogen reacts with oxides of silicon present in the article to transform the oxides of silicon to silicon nitride.

5 more elements